UPVC疲劳及损伤性能探究.doc

UPVC疲劳及损伤性能探究 　　摘要： 参照金属材料疲劳裂纹扩展速率试验方法，采用材料疲劳试验机对硬聚氯乙烯材料进行了Ⅰ型疲劳裂纹的扩展速度及裂纹扩展机理的研究，测试得到了疲劳裂纹扩展长度下所对应的循环次数，进而用割线法得出da/dN，再与ΔK拟合得到疲劳裂纹扩展速率图。接着选取了4 个典型的断面区域进行扫描电子显微镜拍照，得到了4 ?N断面显微组织并进行断面形貌分析 Abstract： Based on the test method of fatigue crack growth rate of metallic materials， the fatigue crack growth rate and crack propagation mechanism of Type I fatigue crack of rigid polyvinyl chloride （PVC） are investigated by the material fatigue testing machine. The numbers of cycles corresponding to fatigue crack length growth are recorded during the text. And da/ dN is obtain by the secant method. Then， it is fitted with ΔK to obtain fatigue crack growth rate. Finally， four typical cross section areas are selected for scanning electron microscope to get the microstructures of 4 kinds of sections and analyze the section morphology. 关键词： 硬聚氯乙烯；疲劳损伤；裂纹扩展速率；断面显微组织 Key words： unplasticized polyvinyl chloride；fatigue damage；crack growth rate；microstructure of cross section 中图分类号：TQ325.3 文献标识码：A 文章编号：1006-4311（2017）06-0172-04 0 引言 UPVC又称硬PVC（Unplasticized Polyvinyl Chloride），它是用PVC 树脂作为主要原材料， 在其中添加润滑剂、稳定剂等后再加热， 在制管机中挤压成不同压力等级和各种规格型号的硬质管材。由于其具有重量轻、耐腐蚀、强度较高等优点，因而在供水管道工程的应用方面具有广阔的前景[1] 随着UPVC管应用领域的扩展，使用者对UPVC的综合性能提出了更高的要求。UPVC材料在应力作用下发生损伤、失效和断裂行为是与材料使用年限密切相关的核心问题。作为工程塑料材料使用的UPVC材料损伤断裂过程比金属材料还要复杂，这过程涉及到高分子材料科学基础、弹塑性力学、损伤与断裂力学等力学学科，同时研究其断裂破坏特征和抗破坏性能是能否合理利用UPVC材料并大面积推广的关键因素[2]。到目前为止国内外众多学者对改善UPVC性能以及它的工程应用做了大量的研究[3]-[10]，但是对UPVC材料的力学性能研究特别是疲劳损伤性能的研究始终止步不前，因此对UPVC材料疲劳损伤性能的研究及其在工程领域的应用研究是当前亟待进行的一项课题。对此，笔者通过本文对这种材料的I型疲劳裂纹的扩展速率、扩展机理和断面显微组织进行了全面的分析，并对UPVC材料的疲劳损伤机理进行了较深入的研究 1 实验方面 1.1 原材料 UPVC板材 1.2 主要仪器及设备 材料疲劳试验机：MTS810 型，美国MTS 系统有限公司； 扫描电子显微镜（SEM）：JSM-6510F型，日本电子株式会社 1.3 试样制备 由于UPVC材料没有对应的疲劳裂纹扩展速率实验的国家标准，因此实验参照《金属材料疲劳裂纹扩展速率试验方法》GB-T6398-2000进行，首先将UPVC板材用切割机加工成标准三点弯试件；再用砂轮打磨机打磨得到试件；接着用手工锯在试件上加工出长度为5mm、宽度为2mm的切口；然后再用美工刀在该切口上切出1mm的尖裂纹，制成标准纯Ⅰ型试件，并由此得到210mm×50mm×15mm的试件（详见图1）。然后在试件切口旁约2mm的位置划一道垂直于试件的上下底并平行于切口的直线作为标记，再用放大镜、美工刀和工具尺在直线上画出刻度，最后将初始刻度线与尖裂纹顶端对准 1.4