低分子量幾丁聚醣 甲基纖維素摻合對不織布加工之研究.PDFVIP

低分子量幾丁聚醣甲基纖維素摻合對不織布加工之研究/ a* a b b b 陳建文 、葉松弦 、翁佳慧 、鄭至玲 、賴碩彬 a 崑山科技大學高分子材料系 b 新化高工化工科 E-mail:kwen46@mail.ksu.edu.tw Abstract:Chitosan polymers with various low molecular 二、實驗方法 weights have beenprepared by means of sulfuric acid 2.1 材料與藥品 degradation.Blending the chitosan polymer with methyl 1.幾丁聚醣 （去乙醯化度為85%,試藥級 ） cellulose at different blending ratios, the resulting 2.甲基纖維素試藥級( ) materials (CH/MC) could be applied to the anti-bacterial finishing of PET non-woven textiles. The performances 3.醋酸 試藥級( ) of the CH/MC mixture on the physical and anti-bacterial 4.鹽酸試藥級( ) properties were estimated by FT-IR and TGA 5.氫氧化鈉試藥級( ) 2 measurements.The results show that the chitosan with 6.PET 不織布(厚度 1.0mm 基重150g/m ) low molecular weight revealsanti-bact Its threshold concentration of eria at about 0.5 wt%. The incorporation 2.2儀器設備 of methyl cellulose into the chitosan would increase the 1.拉伸試驗機(HT9102 ，弘達儀器股份有限公司 ) tensile strength of the PET non-woven with the sacrifice 2.傅立葉光譜分析儀(FT-IR ，Bio-Red Digilab FTS-40) of softness. 3.壓吸機 (RAPID) Keywords:chitosan,methylcellulose,non-woven, anti-bacterial 4.重量損失分析儀 (TGA ，Du Pont 2200) 。 5.烘箱 摘要: 本研究利用濃鹽酸降解 製備出不同分子量的幾 6.電子天平 丁聚醣再與甲基纖維素不同比例摻合 ，應用在聚酯不 7. 柔軟度試驗儀(INTECO 45度傾斜) 織布加工上 。經FTIR 、TGA檢測摻合物及拉力測試和 8.撕裂強度測試機(SEISAKUSHO) 抗菌測試探討其不織布抗菌性和物性 。研究結果顯示 9.黏度計(BROOKFIELD) 檢測其摻合物含有低分子量幾丁聚醣及甲基纖維素兩 成份；以低分子量幾丁聚醣濃度 0.5%處理之不織布即