酸性土壤腐蚀对锚索力学性能影响探究.docVIP

酸性土壤腐蚀对锚索力学性能影响探究 　　摘 要：针对成都市某建设项目基坑支护所采用的锚索腐蚀问题，分别将施加预应力钢绞线裸筋、施加预应力注浆空洞缺陷锚索锚筋、未施加预应力钢绞线裸筋和未施加预应力注浆空洞缺陷锚索锚筋试样埋设至人工配制的高腐蚀性土中，在不同时间段内测试4种试样的力学性能，并绘制出力学性能指标随时间的变化曲线。研究成果对于推断一定腐蚀条件下锚索锚筋的断裂荷载及安全评价具有一定的参考价值 关键词：酸性腐蚀土 锚索 力学性能 Abstract： In order to solve the problem of anchorage corrosion in foundation pit support of a construction project in Chengdu， prestressed steel wire strand was applied to the bare tendon， and prestressed grouting hole of anchor cable was applied respectively. And the unconfined grouting cavities were implanted into the highly corrosive soils. The mechanical properties of the four samples were tested at different time intervals and the mechanical properties were plotted with time. curve. The research results have certain reference value for estimating the fracture load and the safety evaluation of the anchor bar under certain corrosion conditions. Key words： Acid corrosion soil； Anchor cable； Mechanical property 成都市某建设项目设3层地下室，基坑深度在±0.00以下14.40 m，设计基础顶面标高为492.35 m，根据《成都地区建筑地基基础设计规范》（DB51/T5026-2001）第11.5.3条确定，该工程基坑安全等级为一级。结合场地周边条件，拟建场地四周均为市政道路，北为龙港路，东为华泰路，南为成泰路，西华甸路，基坑与道路边线距离1～3 m，设计应对周边道路管线进行调查。建议采用排桩+锚索支护，并应加强支护体系整体结构设计。按照成都市安监站文件的要求，锚索应采用扩大头锚索 在26#、38#号钻孔中共取得2件土试样，根据土的化学分析报告，按《岩土工程勘察规范》（GB50021-2001）2009年版第12.2的规定，对场地土中Cl-含量及pH值进行测定，做场地土对锚索腐蚀性能评价（如表1） 通过表1可以看出，土中Cl-含量达到70 mg/kg左右，pH值为6.9，土质偏酸性，对锚索具有轻微腐蚀性 长期处于土体、岩石中的锚索锚筋或多或少都会受到不同程度的腐蚀，从而影响其使用寿命。锚筋长期浸泡在水中，由于氧溶入较少，不易发生电化学反应，锚筋不易被腐蚀，但干湿交替与存在Cl-的环境对锚索锚筋腐蚀影响极大，其基本原接近，试验场地定在附近边坡坡脚。为缩短腐蚀周期，通过加入NaCl和HCl，提高实验所用土的腐蚀等级，HCl用于控制腐蚀土的pH值 原始土样含水量8.14%，pH值6.9 腐蚀性物质含量为Cl-：365 mg/kg，SO24-：6 383 mg/kg；折算后的Cl-含量为：365+6383×0.25=1960.75 mg/kg，腐蚀等级为中等。根据计算，向每1 kg原始土样中加入15 g的NaCl，使折算后Cl-的含量大于7 500 mg/kg强腐蚀环境土的要求；再加入一定量的HCl及适量的水，使腐蚀土处于酸性环境中，加入量根据试验确定 实验用土配制好后，取3组样品进行腐蚀性测定，其中腐蚀性离子含量如下：Cl-：11 575 mg/kg，SO42-：3 427 mg/kg，含水量20%，pH值为6.74，符合强腐蚀等级土的要求 试验用锚筋采用单孔锚筋1φ15.24mm，其标准强度为1 860 MPa，由高强度低松弛预应力钢绞线制作，设计的试验类型及组数如下 （1）原状钢绞线1组（3根/组） （2）未施加预应力的钢绞线裸筋9组（3根/组），未施加预应力的注浆空洞缺陷锚索9组（3根/组） （3）施加预应力的钢绞线裸筋9组（5根