ALC墙板填充墙裂缝成因试验探究.doc

ALC墙板填充墙裂缝成因试验探究【摘要】随着我国城市化进程的加快及建筑房地产业的蓬勃发展，ALC墙板越来越多的应用于工程项目中，但是由于ALC墙板的自身特性，墙体易出现各种裂缝。基于此，本文结合填充墙裂缝调查情况，从裂缝可能产生的原因入手，着重对ALC墙板填充墙变形进行了试验研究，分析龄期、含水率、温度以及湿度对墙体变形的影响，以便找出ALC墙板填充墙开裂的根本原因。? 【关键词】填充墙；裂缝；收缩变形；龄期；ALC墙板?? Tests on the reason of ALC Wallboard infill wall cracks? Yang Pei-dong?1,Liu Yan-lei?1,Zhao Guang-bo?2,Ren Hong-wei?1,Huang De-qiang?1? (1.Qingdao Technological UniversityQingdaoShandong266033；? 2.Jian Qingdao Construction GroupQingdaoShandong266033) ? 【Abstract】With flourish development of urbanisation and real estate,there are an increaning number of ALC wallboard applied in projects,but the ALC wallboard is apt to cracks due to its own characters.On the basis of this,starting with the reasons of cracks from infill wall crack investagation,tests of ALC wallboard infill wall including age、water content、tempreture and humudity are carried out to find how these factors influence wall deformation,and thus find the root reason of ALC wallboard infill wall crack.? 【Key words】Cracks;ALC wallboard;Age;Opening;Shrinkage deformation?? 1. 引言? 近年来，随着建筑业的迅速发展和墙体材料改革的进行，ALC墙板在各类建筑中广泛应用，同时ALC墙板填充墙裂缝问题日益严重。尤其是住房制度改革以后，随着住宅的商品化，消费者对填充墙裂缝等建筑质量问题更加关注。墙体出现裂缝不仅影响了建筑的美观、墙体的整体性能，还会进一步影响建筑物的使用寿命。因此，ALC墙板墙体开裂问题成为制约ALC墙板工程应用的关键技术问题，分析其裂缝产生的原因，并制定相应的防治措施，是一个需要迫切解决的问题。? 2. 试验目的? 本次试验主要有以下两个目的：? （1）ALC墙板试验的目的是研究其自身变形性能，查找龄期、含水率对其变形的影响。? （2）ALC墙板填充墙试验的目的主要是研究墙体的变形规律，特别是探讨墙体变形的影响因素。? 3. 试验方案? 本次试验记录了9块ALC墙板、6片ALC墙板填充墙的变形量。其中，1#墙体～2#墙体为09月19日安装；3#墙体～4#墙体为08月20日安装；5#墙体～6#墙体为09月10日安装；1#、2#墙体为龄期达到28天的ALC墙板采用管卡法固定由1:3水泥砂浆嵌缝而成；3#、4#墙体为龄期分别为10天、20天的ALC墙板采用管卡法固定由1:3水泥砂浆嵌缝而成；5#、6#墙体为龄期达到28天的ALC墙板采用加固角钢由1:3水泥砂浆嵌缝而成，墙体带有窗洞口。墙体尺寸均：宽×高为4200mm×3000mm（开孔窗洞口为1200mm×1800mm）。? 3.1构件 本次墙体变形量试验的构件主要有五大组（ALC墙板规格：3000mm×600mm×100mm）。? （1）通过观测刚出厂（龄期为0天）的三块ALC墙板变形值、找出ALC墙板自身的变形规律，探讨嵌缝的时间，查找温度、湿度、龄期对ALC墙板变形的影响。? （2）通过观测龄期达到28天三块ALC墙板（不加水和加10%水）的变形规律，查找温度、湿度、含水率及受潮后的二次变形对ALC墙板变形的影响。? （3）通过观测龄期达到28天的两片ALC墙板填充墙在有约束条件下墙体的变形规律，探讨嵌缝的时间，查找在有约束条件下温度、湿度、龄期