空气电极催化剂的掺杂改性.pdfVIP

空气电极催化剂的掺杂改性 谷 鹏，杨占红，李景威，毛 英，彭英彪 (中南大学化学化工学院，湖南长沙 410083) 摘要：研究了在空气电极的催化层中添加其它化合物对锰系催化剂的影响，并在碱性介质中以金属铝为阳极组成碱性 铝一空气电池，考察了电池的放电性能。实验结果表明，NiSO 和La。O。作为催化层的添加剂可以提高催化剂对氧气还 原的催化活性，是空气电极较理想的添加剂，并通过正交实验得出高性能催化剂的最佳制备条件。 关键词：空气电极；MnO 催化剂；稀土；添加剂 中图分类号：TM 911．41 文献标识码：A 文章编号：1002—087 X(2007)12—0991—04 Doping modification of air electrode catalyst GU Peng，YANG Zhan—hong，LI Jing—wei，MAO Ying，PENG Ying—biao (College ofChemistry and Chemical Engineering,Central South University,Changsha Hunan 410083，China) Abstract：The effect of the compounds on ai r electrode was observed by adding some compounds to catalytic layer of the air electrode．The properties of aluminum—air battery with air electrodes were tested．The experimental results show that NiSO4 and La203 can improve the catalytic activity of air electrodes and enhance the discharge voltage of alum num—air battery． They are ideal additives for catalyst of air electrodes． The optimal composition of MnO。 catalyst added bV La，0s in air electrode was obtained by o~hogonal method． Key words：air electrode；MnO，electro catalyst；rare—each；additive 铝一空气电池原材料丰富，性能价格比高，且尢污染，被 到混合物有弹性，用压片~JLCPg压至所需厚度：防水透气层采用 称为是“21世纪的绿色能源”…：但是，目前铝．空气电池还 质量比为1：1的活性炭和乙炔黑混合物，以乙醇分散，加入 存在很多问题，尤其是空气电极催化剂大多采用贵金属化合 占防水层总质量60％fl~q PTFE乳液，再仿照催化层的制作方 物，成本高，一直限制_r其商业应用。随着便携式电子产品的 法来制成防水透气层 发展，世界范闱内掀起了空气电池的开发热潮，寻找… 种既经 实验中以泡沫镍作为空气电傲的集电体，采用催化层+ 济又耐朋的空气电极催化剂，成为电化学T作者和催化剂研 集电体+防水透气层的排列方式制作电极，电极大小为4 究者的一个目标l1_：锰氧化物具有良好的氧还原和过氧化氢分 ClTI2。 斛催化活性，行且价格低廉、丰富易得，目前已成为空气电檄 1．3极化性能测试 催化剂的研究热点l 3_。本史对MnO 催化剂进行了几种化合物 采用镍片作辅助电极的经典 电极体系，用CHI 660型 的掺杂，通过研究其做化曲线和放电曲线，发现在锰氧化物催 电化学工作站在室温下测试空气电极的稳态极化曲线。极化 化剂中掺杂部分化合物能提高空气电极的催化活性。