89mm连轧管机组荒管椭圆度产生原因分析_邓丕安.pdfVIP

40 质量控制 Φ89 mm 连轧管机组荒管椭圆度产生原因分析 邓丕安，成克武 （衡阳华菱钢管有限公司，湖南 衡阳 421001 ） 摘 要：分析了半浮动芯棒连轧管机组连轧荒管椭圆度过大的产生原因，认为其连轧荒管椭圆度过大是芯棒 润滑不良、工模具表面质量欠佳、工艺参数调整不当等多种因素共同作用的结果。通过改善芯棒润滑条件和合理 分配变形量可有效减小连轧荒管的椭圆度。 关键词：连轧管机组；荒管；椭圆度；产生原因；分析；措施 中图分类号： 文献标志码： 文章编号： （ ） TG335.71 %% B % 1001-2311 2011 05-0040-03 Analysis of Causes for Ovality of Shell as Rolled by Φ89 mm Mandrel Mill ’ ， Deng Pi an Cheng Kewu （ ， ， ， ） Hengyang Valin Steel Tube Co. Ltd. Hengyang 421001 China ： - Abstract Analyzed the elements responsible for the excessive ovality of the shell as rolled by the semi floating mandrel mill. As a result ，it is concluded that the problem of the said excessive shell ovality is brought about jointly by such elements namely ，insufficient lubrication of the mandrel ，poor surface quality of the operational tools ，and improper setting of the process data. Accordingly ，the ovality can be well reduced by means of better - ing the lubrication conditions of the mandrel ，and appropriately distributing the deformation amounts. Key words ：Mandrel mill ；Shell ；Ovality；Cause；Analysis ；Measures 连轧管机组是一种高效生产无缝钢管的轧管机 的影响，导致荒管在成品机架上的宽展过大 （或过 组，其实质是将穿孔后的毛管套在一根长芯棒上， 小），使得最终轧出的荒管外径偏离人们所希望的 通过多个（一般为 个）互成 连续布置的二辊 结果，给后续张力减径工序带来不便，严重时甚至 5~9 90° 式或三辊式轧管机对钢管进行轧制，从而实现无 造成钢管报废。投产后，由于对荒管椭圆度过大的 缝钢管生产的高度机械化和自动化。与其他无缝钢 危害性认识不足，在生产过程中因荒管椭圆度过大 管生产机组相比，连轧管机组具有优质、高产、低 而引起生产停车及产品报废的现象时有发生。因 耗等优势，自 世纪 年代以来，在世界各国 此，研究连轧荒管椭圆度过大的产生原因对连轧管 20 50 得到了广泛应用。根据芯棒运动方式的不同，连轧 机组的生产意义重大。 管机组分为全浮动、半浮动和限动芯棒 类，本