降低铝脱氧钢连铸水口结瘤的研究论文.pdfVIP

钢技术 2017 年第2 期 ANGANG TECHNOLOGY 总第404 期 降低铝脱氧钢连铸水口结 的研究 黄玉平 郭庆涛 唐雪峰 吕春风 廖相巍 钢集团钢铁研究院,辽宁鞍山 114009) 摘要 对连铸铝脱氧钢生产中存在的浸入式水口结瘤问题进行了分析研究, 认为钢液中 的Al O 夹杂蓄积在水口内壁是水口结瘤的主要原因。 开发出了新型精炼渣应用于LF 精炼, 2 3 结果表明,采用新型精炼渣可有效地减少连铸铝脱氧钢的水口结瘤问题。 关键词 连铸；水口结瘤；氧化铝；精炼渣 中图分类号 TF769 文献标识码 A 文章编号 1006-4613(2017)02-0017-03 Study on Reducing Clogging at Submerged Entry Nozzle in Continuous Casting Molten Aluminum Deoxidation Steel Huang Yuping Guo Qingtao Tang Xuefeng Lv Chunfeng Liao Xiangwei （Iron Steel Research Institutes of Ansteel Group Corporation, Anshan 114009, Liaoning, China） Abstract The problem of clogging at submerged entry nozzle in continuous casting molten aluminum deoxidized steel was analyzed. It was concluded that the Al O inclusions accumulated at 2 3 the inner wall of the submerged entry nozzle was the main cause leading to clogging at submerged entry nozzle. The new type of the refining slag was developed and used for refining in LF. The results showed that the new developed slag can effectively reduce the clogging at submerged entry nozzle in continuous casting molten aluminum deoxidized steel. Key words continuous casting; clogging at submerged entry nozzle; alumina; refining slag 连铸技术以其成本低﹑生产效率高﹑节约能源 目前这方面尚无能够成功应用于生产的研究成 和铸坯质量好等优势 到迅速发展 但连铸机浸 果。 本文对鞍钢股份有限公司炼钢总厂厚板坯连 入水口结瘤堵塞的问题始终未 到彻底解决 成 铸机浸入式水口结瘤情况进行了调查分析 尝试 为提高连铸生产效率的限制环节之一。另外 水口 在精炼工序采用新型精炼渣降低钢液中的Al2O3 结瘤还带来许多质量问题 如水口内结瘤物会引 夹杂含量来解决结瘤问题 并进行了实验研究。 起偏流和结晶器液位波动 剥落的结瘤物上浮滞 留在钢液里等 均使铸坯产生表面和内部缺陷