fabrication and characterization of hap al2o3 composite cating on titanium substrate制备和表征hap氧化铝复合钛衬底介质.pdfVIP

J. Biomedical Science and Engineering, 2008, 1, 190-194 Fabrication and characterization of HAp /Al O 2 3 composite cating on titanium substrate Zhou-Cheng Wang, Yong-Jin Ni, Jin-Cong Huang Department of Chemical and Biological Engineering, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen, China. Correspondence should be addressed to Zhou-Cheng Wang (zcwang@). Received July 5, 2008; revised September 28, 2008; accepted September 28, 2008 ABSTRACT substrate by the application of electric field [7]. EPD has recently gained increasing interest in the processing of HAp/Al O composite coating was fabricated 2 3 advanced ceramic materials and coatings not only be- onto micro-arc oxidized titanium substrate cause of its coast-effectiveness requiring simple appara- using a combination of electrophoretic depo- tus, but also it offers important advantages in the deposi- sition and reaction bonding process. SEM, tion on substrates of complex geometry [8]. As for many EDS and XRD were employed to characterize ambient-temperature powder coating processes, the de- the titanium substrate and as-prepared coat- posit is in the form of a loosely packed particles which ings. The interfacial bonding strength of