characterization and electromagnetic studies on nizn and nicuzn ferrites prepared by microwave sintering technique特性和电磁研究nizn和nicuzn铁氧体由微波烧结技术.pdfVIP

Materials Sciences and Applications, 2012, 3, 628-632 /10.4236/msa.2012.39091 Published Online September 2012 (http://www.SciRP.org/journal/msa) Characterization and Electromagnetic Studies on NiZn and NiCuZn Ferrites Prepared by Microwave Sintering Technique 1 1* 1 2 Matli Penchal Reddy , Il Gon Kim , Dong Sun Yoo , Wuppati Madhuri , Nagireddy Ramamanohar Reddy3 2 2 , Kota Venkata Siva Kumar , Rajuru Ramakrishna Reddy 1Department of Physics, Changwon National University, Changwon, South Korea; 2Department of Physics, Sri Krishnadevaraya University, Anantapur, India; 3Department of Materials Science and Nanotechnology, Yogi Vemana University, Kadapa, India. * * Email: igkim@changwon.ac.kr, drlpenchal@ Received April 24th, 2012; revised June 3rd, 2012; accepted July 14th, 2012 ABSTRACT The low-temperature sintered NiZn and NiCuZn ferrites with the composition of Ni Zn Fe O and Ni Cu Zn 0.40 0.60 2 4 0.35 0.05 0.60 Fe O were respectively synthesized by the microwave sintering method. These powders were calcined, compacted and 2 4 sintered at 950˚C for 30 min. X-ray diffraction (XRD) patterns of the samples indicate the formation of single-phase cubic spinel structure. The grain size was estimated from SEM images which increase with CuO addition. The X-ray density is higher than the bulk density in both the ferrites. The temperature variation of the initial permeability of these samples was carried out from 30˚C to 250˚C. The NiCuZn ferrite had higher initial permeability than that