动态再结晶过程的元胞自动机模拟.pdfVIP

下半月出版 Material Heat Treatment 料热处理技术 动态再结晶过程的元胞自动机模拟 麻晓飞 (临沂大学 工学院, 山东 临沂 276005) 摘 要 结合金属热加工过程的冶金学原理 基于非均匀分布的位错密度场 建立了动态再结晶二维元胞自动机模 型(Cellular Automaton) 并对不同应变速率和不同变形温度条件下的 态再结晶过程进行了模拟遥 结果表明院动态再结 晶存在明显的孕育期曰再结晶晶核优先在晶界处产生曰提高变形温度或者降低应变速率均能促进动态再结晶的进行遥 关键词 元胞自动机曰 态再结晶曰微观组织演化 中图分类号 TG 111;TP391 文献标识码 A 文章编号 Simulation on Dynamic Recrystallization Using Cellular Automaton Method MA Xiaofei (Engineering College, L inyi Univ ers ity, L inyi 276005, China) Abstract 院Based on the fundamental metallurgical principles of metal plastic forming, two dimensional cellular automata models for the dynamic recrystallization were built. The dynamic recrystallization process under different hot working temperature and strain rate was studied. The results show that there is an obvious incubation period at the beginning of dynamic recrystallization. The recrystallization nuclear preferentially concentrates at the grain boundaries. The recrystallization processing could be promoted with the increase of temperature and decrease of strain rate. Key words 院cellular automaton; dynamic recrystallization; microstructure evolution 态再结晶是金属热变形过程中非常重要的微 型均做了以下假设院 在模拟初始阶段位错大多均匀 观组织演变过程 它直接对其最终组织状态产生影 分布 没有考 晶界对位错增值的影响曰将再结晶晶 响 同时也是决定其内部晶粒尺寸及其分布的关键 核人为的设置在晶界处 而没有考 位错的大小对 因素之一 在很大程度上决定了产品的最终微观组 形核位置的影响 从而影响了模型的模拟精度遥 织和力学性能遥 因此 在工业生产之前 了解热变形 本文在现有 态再结晶模型的基础上 对初始位错 过程中 态再结晶发生的机理尧 规律及其相应的材 的分布作了改进 引入非均匀分布的位错密度场 建 料组织结构变化 可为制定合理工艺以得到理想的 立了 态再结晶元胞自动机模型 并对不同变形温 [1] 度和不同应变速率下的