硫酸法烷基化装置存在的腐蚀问题原因分析及解决措施.pdfVIP

硫酸法烷基化装置存在的腐蚀问题 原因分析及解决措施 曲　豫 (大连西太平洋石油化工有限公司，辽宁大连 116600) 摘  要 ：某石化公司烷基化装置停工十余载重新开启后，一年时间暴露出一系列腐蚀问题， 通过走访和调研国内若干采取硫酸法做催化剂的企业进行对比和深入分析，找出腐蚀问题的原因 个根源，并相应提出针对性的防腐措施，计划在检修期间予以逐项实施。 关键词： 硫酸法烷基化装置　酸腐蚀　原因分析　治理措施 中图分类号：TE98 文献标识码：A DOI：10.13726/j .cnki.11-2706/tq.2015.07.071.03 Causes Analysis and Solving Measures of the Corrosion Problems on Sulfuric Acid Alkylation Unit QU Yu (Dalian west pacific petrochemical company, Dalian 116600, China) Abstract: The alkylation plant of one refinary has been shutdown for tens years, and then re-start- up. For a year operation, it exposed a series of problems of corrosion. This paper finds out the reason which causes corrosion problems by visiting, investing, comparing and analysising several domestic enterprises who take sulfuric acid method as catalyst, and proposes corresponding anti-corrosion measures to be carried out during overhaul one by one. Key words: sulfuric acid alkylation; acid corrosion; cause analysis; rectify measures 0 引言 大连某石化公司烷基化装置引进美国STRATCO 公司专利技术—采用卧式偏心高效反应器和反应流 出物致冷工艺，于1998年9月开工，1999年6月装置 停工退料处理，20 13年10月烷基化装置重新检修投 产运行，至今已连续运行一年，暴露腐蚀问题较 多，严重影响了装置的平稳运行，针对此项问题， 通过请进专家帮助分析、走出去进行实地调研的办 法，立足于国内硫酸法烷基化所暴露出的腐蚀问 题，进行了纵深剖析，着眼于运用检修期间力求消 除瓶境间间 办 响 作者简介：曲豫，高级工程师，硕士，长期从事炼化企业设备管理工作。 全面腐蚀控制 71 第29卷第07期2015年07月 腐蚀研究 Corrosion Research 进料处由于管线设计布局原因，瞬间会出现较大湍 该公司烷基化腐蚀主要表现为酸、硫酸酯分解 流，存在冲刷腐蚀。 产生的亚硫酸腐蚀；温度和流速未能按照原始设计 1.2 设备方面 操作也是重要的影响因素。