2纳米颗粒光催化降解甲醛条件优化-- TiO2纳米颗粒光催化降解甲醛条件优化.docVIP

2纳米颗粒光催化降解甲醛条件优化’ TiO2纳米颗粒光催化降解甲醛条件优化 　　摘要：针对甲醛污染的问题，以锐钛矿型TiO2纳米颗粒为催化剂对甲醛进行光催化降解，主要研究了光照时间、甲醛稀释倍数及H2O2浓度对甲醛降解率的影响。结果表明，甲醛的降解率随时间增加而增加，二者表现为近似线性的关系；当甲醛稀释倍数为2 000，H2O2浓度为300 mg/L时，甲醛的降解率最高。 关键词：TiO2纳米颗粒；光催化降解；甲醛；条件优化 中图分类号：X788 文献标识码：A 文章编号：0439-8114（2013）12-2800-03 Optimization of Photocatalytic Degradation Condition of Formaldehyde by TiO2 Nanoparticals ZHANG Hong-mei，KONG De-guo，LUO Hua-ping （College of Mechanic and Electrical Engineering，Tarim University，Alar 843300，Xinjiang，China） Abstract： In view of the formaldehyde pollution，anatase TiO2 nanoparticals were used as photocatalyst to degradate formaldehyde. The effects of illuminative time， dilution ratio of formaldehyde and the concentration of H2O2 on the degradation rate of formaldehyde were studied. The results indicated that the relationship between the degradation rate of formaldehyde and the illuminative time was linear. When the dilution ratio of formaldehyde was 2 000 and H2O2 was 330 mg/L， the degradation rate of formaldehyde was the highest. Key words： TiO2 nanoparticals； photocatalytic degradation； formaldehyde； condition optimization 甲醛是室内装修带来的主要污染物之一，其对人类健康的危害不容忽视。甲醛对孕妇和婴儿的危害更为严重，国际癌症机构已经将甲醛确定为可疑致癌物[1-5]。因此，如何快速便捷地清除甲醛成为一项重要的任务。常用的净化甲醛的方法主要有：植物吸附法、通风法、活性炭吸附法及化学法[6]。由于通常的吸附方法只能将甲醛转移而不是分解，因此，甲醛的毒性并未消除。TiO2纳米颗粒由于有大的比表面积、无毒、成本低，并且能将甲醛分解成无毒的CO2和H2O，因此，在环境净化中应用前景广阔[7-12]。鉴于此，用锐钛矿型TiO2纳米颗粒对甲醛进行光催化降解，希望能够为环境净化提供理论依据。 1 材料与方法 1.1 材料 1.1.1 试剂 锐钛矿型TiO2纳米颗粒，浙江泓晟纳米科技股份有限公司；40%甲醛溶液，分析纯，洛阳昊华化学试剂有限公司；乙酰丙酮，分析纯，郑州中天实验仪器有限公司；醋酸铵，分析纯，郑州中天实验仪器有限公司；去离子水，自制。 1.1.2 主要仪器 721型紫外-可见分光光度计；表面光电压谱仪。 1.2 方法 1.2.1 光照时间对甲醛降解率的影响 将一定量的TiO2纳米颗粒超声分散到50 mL稀释1 000倍的40%甲醛溶液中，紫外光照射下，每30 min取样一次，采用分光光度法测定甲醛的吸光度。 1.2.2 甲醛稀释倍数对降解率的影响 将0.05 g TiO2纳米颗粒分别超声分散到50 mL稀释500倍、1 000倍、1 500倍、2 000倍和2 500倍的40%甲醛溶液中，紫外光照射一段时间后取样测定甲醛的吸光度。 1.2.3 H2O2浓度对甲醛降解率的影响 将0.05 g TiO2纳米颗粒超声分散到50 mL稀释1 000倍的40%甲醛溶液中，滴加H2O2配制浓度分别为66、132、198、254和330 mg/L的溶液，紫外光照射1.5 h后，采用分光光度法测定甲醛的吸光度。 2 结果与分析