聚羧酸系-萘系高效减水剂和水泥相容性探究.docVIP

聚羧酸系\萘系高效减水剂和水泥相容性探究 　　摘要：由于原材料的不同，同强度等级的水泥配制的混凝土性能存在着较大的差别。目前市场上的高效减水剂对不同厂家的水泥存在着相容性的问题，影响混凝土拌合物的和易性。本文选用聚羧酸系高效减水剂HK01、ZS01和萘系高效减水剂NSF-2与三种不同产地的P·O42.5水泥进行对比试验，测定了水泥浆体流动度及30分钟、60分钟的经时变化，结果显示聚羧酸系高效减水剂HK01、ZS01与三种水泥有良好的相容性，且减水效果显著，而萘系高效减水剂NSF-2的相容性就要差些。另外，减水剂的掺入法对水泥浆体的流动度有较大的影响。 关键词：高效减水剂；水泥；相容性 Abstract: Due tothe different raw materials,the performance of concretepreparedwith the same strength gradecementexist in the larger differences. Currently on the marketof super plasticizer oncement indifferentcompatibilityproblems,affectingconcrete workability.In this paper,usingpolycarboxylates efficient contrast test ofP#8226; O42.5cementagent HK01,ZS01 and naphthalene super plasticizerNSF-2 and threedifferent places,change of cementpastefluidity and30 minutes,60 minutesafterthetest,results showed thatpolycarboxylate super plasticizerHK01,ZS01andthree the cementhas good compatibility,anddecrease water effect is remarkable,andthe naphthalene water-reducing performancewillworsecompatibilityagent NSF-2.In addition,water-reducing agentofcement pastefluidity influence. Key words:super plasticizer;cement;biocompatibility 中图分类号：TU5 文献标识码：文章编号: 1 引言 高效减水剂对水泥有强烈分散作用，能大大提高水泥拌合物流动性和混凝土坍落度，同时大幅度降低用水量，显著改善混凝土工作性。能增强混凝土的抗渗、抗冻融及耐腐蚀性，提高了混凝土的耐久性。 采用高效减水剂技术制备的高性能混凝土,广泛应用于高层建筑、大型堤坝、桥梁、隧道、轨枕构件等建设工程中，在经济建设和社会发展中发挥重大作用。在保证质量的前提下，能够较大幅度地减少水泥用量，不仅产生良好的经济效益，又因间接地减少碳排放而友好于我们生存的环境。 由于各地生产水泥的原材料存在差别，水泥性能变化比较大，高效减水剂对于不同水泥存在着相容性问题，以致如果减水剂使用不当，不仅达不到预期效果，而且还可能产生工程质量事故，造成巨大损失。因此，随着混凝土技术的提高，水泥和高效减水剂之间的相容性问题引起越来越多的关注，工程施工前了解和验证减水剂与水泥的相容性也因此成了不可缺的准备工作。 为此，本文选用高效减水剂聚羧酸系HK01、聚羧酸系ZS01、萘系NSF-2以及三种不同产地的水泥，通过测定水泥浆体的流动度和经时变化，探讨了两种高效减水剂与水泥之间的相容性问题。 2试验材料与试验方法 2.1试验材料 水泥：邯郸Ｐ·Ｏ４２．５水泥（Ｃ－１），朔州金圆Ｐ·Ｏ４２．５水泥（Ｃ－２），阳泉冀东Ｐ·Ｏ４２．５水泥（Ｃ－３）； 高效减水剂：聚羧酸系高效减水剂HK01（含固量15%），聚羧酸系高效减水剂ZS01（含固量15%）,萘系高效减水剂NSF-2（含固量15%）。 2.2试验方法 水泥净浆流动度测试： 采用水泥净浆搅拌机、截锥试模（上口直径36mm，下口直径60mm，高度60mm）、玻璃板、秒表、钢直尺等工具对掺加高效减水剂水泥浆的流动度进行测定。先将玻璃板放在水平位置，用湿布抹擦玻璃板、截锥试模、搅拌器、及搅拌锅，使其表面湿而不带水渍。将截锥试模放在玻璃板中央，并用湿布覆盖待用。接下来将搅拌好的水泥浆体置入截