Langmuir surface area, 1100m2/g, BET surface area, 914m2/g Pore volume, 0.39cm3/g N2 adsorbed in the pore, 337mg/g Bai, J. F. Chem. Commun., 2009, 7551-7553 A small cage 8.5 ang A large pore 8.8*21.5 ang MOF-505 analog.Cu2(EBTC) Langmuir surface area 2844m2/g BET surface area 1852m2/g 286cm3/g H2 at 77K 2.58wt% 178cm3/g CO2 at 273K 252cm3/g C2H2 at 273K C2H2 Bu, X.H., Chem. J. Eur., 2008, 2771-2776 The selective sorption of O2 and CO2 over N2 Diameter, O2 3.46 ?; CO2 3.3 ?; N2 3.64 ?; H2 2.8 ?; CO 3.76 ? 79.3cm3/g O2 at 77K 98.8cm3/g CO2 at 195K Langmuir surface area 279 and 390m2/g for O2 and CO2; BET surface area 246 and 313m2/g for O2 and CO2 MOF作为发光材料 Representation of emission possibilities in a porous MOF Structure and luminescence properties of Zn3L3(DMF)2(left) and Zn4OL3(right) [Cd3L6](BF4)2(SiF6)(OH)2+13.5H2O L is 2,6-di(4-triazolyl)pyridine Luminescence spectra of complexes with increasing dehydration and partially rehydrated Cu6L6+H2O+DMSO, 1D nanotubular channels 1.2nm L is 5,6-diphenyl-1,2,4-triazine-3-thiol Luminiscence spectra of the porous solid and after Immersing this solid in an aqueous solution of toluene [Eu(pdc)1.5(dmf)](DMF)0.5(H2O)0.5 pdc is pyridine-3,5-dicarbrate Cu(NO3)2 at different concentration Comparison of different metal ions Coordination to metal a, 1D InO4(OH)2 Chain in 1 b, four TBAPy to an In(III) c, eight In to one TBAPy d,e,f, 3D view along [001] [010] directions In(NO3)3 850C DMF+dioxane+H2O [In2(OH)2(TBAPy)]+guests 1 * 奇妙的金属有机骨架材料 Magic Metal-Organic Frameworks 根据联合国政府间气候变化专门委员会（IPCC）规定，目前由人类活动引起的大量聚集在大气中的温室气体主要是二氧化碳、甲烷、一氧化氮、六氟化硫和两组工业气体氢氟烃(HFCs)和全氟烃(PFCs) 温室气体效应 环境污染与能源危机 解决办法 1，捕获并存储排放的气体 2，开发基于氢的清洁能源 新材料存储 金属有机骨架材料MOFs 什么是金属有机骨架材料MOFs ？ Cu Ag 配体的种类 金属有机骨架材料MOFs的奇妙之处： 有大的表面积与质量比，能象海绵吸水那样吸收大量气体，比沸石和活性碳好，能用于气体存储、气体分离。 能用作传感器、缓释药品的给药载体。 能用作发光材料、磁性材料。 能将存储功能与催化作用结合，将捕获的二氧化碳转化为有用的燃料如甲醇，能用作车载储氢材料 国际能源暑（IEA）提出的氢能源实用化的目标： 质量储氢率5%，体积储氢率50g/L， 美国能源部（DOE）提出的氢能源实用化的目标： 质量储氢率6.5%，体积储氢