低周反复荷载下再生混凝土框架中间节点的受力性能.docx

低周反复荷载下再生混凝土框架中间节点的受力性能彭有开1 ，吴徽2 ，梁能山3 ，焦志超2 ，高全臣1( 1． 中国矿业大学( 北京) 力学与建筑工程学院，北京 100083; 2． 北京建筑大学工程结构与新材料北京市高等学校工程研究中心，北京 100044; 3． 城市建设研究院，北京 100120)摘 要: 对足尺的 3 个再生混凝土框架中间节点与 1 个普通混凝土节点进行低周反复荷载试验，主要目的为考查在低轴压比情况下再生混凝土节点发生粘结滑移破坏的可能性。各试件符合“强柱弱 梁、强节点”的设计原则。结果表明，在低轴压比情况下，再生混凝土节点试件发生显著的粘结滑移， 延性性能和耗能性能差，不能满足抗震设计的要求，而相应的普通混凝土节点实现了梁铰破坏机制， 延性和耗能性能良好。为获得良好的抗震性能，应对再生混凝土节点区锚固进行合理设计，如采用 可靠的机械锚固措施，建议进一步开展再生混凝土框架节点区粘结机理和锚固措施研究。关键词: 再生混凝土; 中间节点; 抗震性能; 粘结滑移中图分类号: TU375． 4文献标志码: ABehavior of Ｒecycled Concrete Interior Beam － column Joints under Cyclic LoadingPENG Youkai1 ，WU hui2 ，LIANG Nengshan3 ，JIAO Zhichao2 ，GAO Quanchen1( 1． School of Mechanics and Civil Engineering，China University of Mining and Technology ( Beijing) ，Beijing 100083，China; 2． Beijing Higher Institution Engineering Ｒesearch Center of Civil Engineering Structure and Ｒenewable Material，Beijing University of Civil Engineering and Architecture，Beijing 100044，China; 3． China Urban Construction Design and Ｒesearch Institute，Beijing 100120，China)Abstract: Three full － scale recycled concrete interior joints and one normal concrete joint are tested under cyclicloading． The tests aim at examining the possibility of bond failure in recycled concrete interior joints with low axial load ratios． All specimens are designed following the design philosophy of strong column － weak beam and strong joint approach． The results show that significant bond slip occurs in recycled concrete joints under low axial load ra- tios． They exhibit low ductility and energy dissipation which can not meet the requirements of seismic design． How-ever，the corresponding normal concrete specimen achieves beam hinge mechanism and gains good ductility and en-ergy dissipation． In order to attain satisfactory seismic performance，it is suggested that the anchorage detailing should be reasonably designed for recycled concrete joints，such as taking reliable mechanical anchorage． It is rec- ommended that the bond mechanism and anchorage me