Bi系超导带材加压扩散连接研究.pdfVIP

IFWT’2004 航空航天焊接国际论坛 Bi系超导带材加压扩散连接术 邹贵生1 胡乃军1 吴爱萍1 张德库1 任家烈1 韩征和2李明亚2顾晨2 易汉平3 (1清华大学机械工程系北京100084) (2清华大学应用超导研究中心北京100084) (3北京英纳超导技术有限责任公司北京 100176) 摘要：采用先冷压成形再高温无压退火和高温直接加压退火两种工艺扩散连接Bi系高温超导带 材。研究了冷压和高温加压工艺以及退火参数对超导带材连接质量的影响。结果表明，适当的 冷压和高温加压有利于超导芯之间的界面结合和超导电性的提高，并初步获得了接头电性和力 学性能较好的工艺。 关键词：Bi系高温超导带材冷压成形扩散连接超导电性 Abstract：Bi—Sr-Ca-Cu一0 were withtwodiffusion methods． superconductingtapes joined bonding at Thefirstmetllodincludes room andthen inair．Thesecondmethod pressing temperatureannealing isdirect inair．Theeffectsof as with such hightemperatureannealingpressing parameterscooling timeand onthe ofthe were temperature pressing，annealing propertiestapejoints investigated．A suitable ordirect could the between coolingpressing hi曲temperaturepressingimprovebonding COreSand relative wasobtained． electivity superconducting propertiesofjoints．Aoptimaltechnology critical at Keywords：Bi·Sr-Ca-Cu·0high temperaturesuperconductingtapes，Joiningbypressing room temperature，Diffusionbonding，Superconductingelectricity 0前言 Bi系高温超导材料(BsCCO)的线材和带材已进入了实用化研究阶段，而成熟的连 接技术是其获得广泛应用的重要前提之一。根据超导材料连接必须同时满足力学性能和超 导电性的要求，固态扩散连接是最有前景的超导连接方法。 高温超导带材由陶瓷超导芯及其外包套金属Ag或其合金组成，而银及其合金在高温 如800℃左右的塑性较好。当采用一般的扩散连接工艺，即在高温加热的同时施加大的压 力将使包套金属Ag或其合金压入超导芯，从而明显影响接头的超导电性。为此，目前的 扩散连接工艺是：先通过腐蚀外包套以制备扩散连接的搭接窗口，之后，利用Ag及其合 金如Ag—Cu包套在室温时具有良好的塑性，对两个对接好的窗口施加足够大的压应力 +863项目(2002AA306113)子课题和清