连铸板坯夹杂物的综合评定研究.pdf

连铸板坯夹杂物的综合评定 任翠英1 张家泉!’ 韩乃川2 洪建国2 姜家和2 江中块2 吴浩方2 (1北京科技大学2宝钢集团上海梅山有限公司) 摘要：对当前常用的铸坯夹杂物评定手段，如低倍、硫印检测、大样电解、金相显微镜、扫描电镜及图像分析等作 用与效果进行了系统地比较分析。指出实验检测过程中其各自的局限性和可能偏差，并结合实际板坯夹杂物分 析，提出互补分析和综合评定的工艺研究途径。 关键词：连铸板坯夹杂物评定方法 EvaluationofInclusionsin CaStSlabs Comprehensive Continuously Ren Cuiyin91ZhangJiaquanl HanNaichuana Jiahe2 Wu HongJimagu02Jiang JiangZhongkuai2Haofan92 ofScienceand 2BaosteelMeishan (1University TechnologyBeijing Group Co．，Ltd．) methodsfortheevaluationofinclusionsin cast asmacro Abstract：The continuouslyslabs，such eteching，electroilysis， electron and beenevaluatedand accord— metallographicexamination，scanningmicroscope analysis，have compared image totheirfunctions．Theindividuallimitationor ofthemethodshasbeen OUtforthecorrectunder— ing dimdvantage pointed in an totheinclusionsin theoverall ofinclusionsslab as standing steels．Takinganalysis samplesexample，acomprehen— hasbeen siveinclusionsevaluationroute withvariousmentionedabove presented ways interdependly． castslabinelusiOIlSevaluation Keywords：continuously 进行化学侵蚀，利用钢中缺陷和基体侵蚀程度的差异 1引言 来显示铸坯中可能存在的凝固枝晶、缩孔僦松、裂纹、 钢中非金属夹杂物的研究是当前进一步提升钢材质 夹杂、偏析以及白点等缺陷。所用试剂(如浓盐酸)使 量、优化炼钢生产工艺的重要途径。钢中可能存在的各 用时一般有冷、热之分，其侵蚀强度各异。一般而言， 种夹杂物都将不同程度地影响铸坯及其成品的质量，尤 与热蚀剂相比，冷蚀剂酸蚀过程产生的有害气体少，可 其是降低钢材的塑性、韧性、抗