电老化工艺对热双金属元件的稳定性分析 （德力西电气有限公司上海分公司，上海201812 ）鲁礼骏 靳海富 肖裕文 摘要：本文阐述了低压电器中的热双金属元件的电老化工艺对其稳定性的分析， 研究了热双金属元件及组元随着电老化次数的增加，热双金属元件逐渐趋于稳 定状态。通过热双金属元件的工作端初始位置变化的分析，确定其达到稳定状 态所需电老化的次数及相关工艺参数。 关键词：热双金属元件；电老化；残余应力；稳定性 The analysis of electrical aging process of thermal bimetal element on its stability （Delixi Electric Co., LTD.Shanghai Branch , Shanghai 201812 Lu Lijun, Jin Haifu, Xiao yuwen Abstract: This paper describes the analysis of electrical aging process in low voltage electric apparatus of thermal bimetal element on its stability. And with the increase of the number of electrical aging, thermal bimetal element working end of initial position of the steady state. Analyzing the change of working end of the initial position of thermal bimetal element , determine the required to reach the steady state electrical frequency and parameters of aging. Key words: thermal bimetal element; electrical aging; residual stress; stability 1 引言 热双金属元件是由两种或多种不同膨胀系数的金属或合金复合在一起组成 [1] 的具有随温度变化而发生形状变化的复合功能材料 。这种材料广泛应用于低 压电器产品上，如塑壳式断路器、热过载继电器等。热双金属元件在加工成形 的过程中会产生较大的残余应力，在元件焊接、铆接过程中也会产生残余应力， [1] 这些应力是造成热双金属元件工作不稳定的原因之一 。热双金属元件在使用 前需对其残余应力消除处理。本文主要阐述采用电老化工艺对热双金属元件的 稳定性分析。 2 控制热双金属元件的稳定性的意义 稳定性是指热双金属元件在长期应用中，性能是否保持稳定，元件工作端的 移动轨迹是否重复。热双金属元件在使用过程中，经常呈现这样一种现象：当 使用较长一段时间或静止放置一段时间，条形热双金属元件的工作端在电器产 品中不能回复到原来位置。工程技术称之为零点漂移。元件出现零点漂移就会 直接影响产品长延时热过载保护功能的准确性，而其主要原因是元件的不稳定 [2] 性所致 。 为了尽可能的避免热双金属元件在使用过程中出现零点漂移现象，在使用前， [3] 需对元件进行稳定性处理，尽可能的消除热双金属元件的残余应力 。 3 试验材料和方法 电老化是消除热双金属元件的残余应力的一种稳定性处理工艺方法，对热 [4] 双金属元件通以几倍额定工作电流，消除其在加工过程中的残余应力 。 试验材料以某型号的热过载继电器为例，试验环境温度为室温 20 ℃，热双 金属元件牌号为 5J1578，将焊接完好的热双金属元件装配在产品上，并紧