混凝土结构中钢筋锈蚀机理特征及检测评定方法惠云玲.docVIP

——————————————————————————————————————————————— 混凝土结构中钢筋锈蚀机理_特征及检测评定方法_惠云玲 混凝土结构中钢筋锈蚀机理、 特征及检测评定方法 惠云玲 (冶金工业部建筑研究总院　北京　100088) 　　 郭永重 (人民大会堂管理局　北京　100800) 　　 李小瑞 (武汉钢铁(集团)公司　武汉　430083) ,　　摘　要:论述了几种钢筋锈蚀的机理及相应的损坏特征,并提出了钢筋腐蚀混凝土开裂锈蚀量评估方法,　　关键词:钢筋锈蚀　检测　评定方法 ANDEVALUATIONOF CORROSIONINCONCRETESTRUCTURES HuiYunling (CentralResearchInstituteofBuildingandConstructionofMinistryofMetallurgicalIndustry　Beijing　100088) GuoYongzhong (TheAdministerBureauoftheGreatHallofthePeople　Beijing　100800) LiXiaorui (WuhanIronandSteelCompanyGroup　Wuhan　430083) Abstract:Thispaperdescribesthecorrosivemechanismandcorresponingdamagecharacteristicsofseveralreinforcements;gives appearancecheckmethodandpotentialamp;resistanceevaluationmethodsofthereinforcementcorrosion;proposestheassessmentmethodofthecorrosivedegreeofconcretecrackingbyreinforcementcorrosion,whichmaybeareferencefordurabilityevaluationofconcretestructures. Keywords:reinforcementcorrosion　detection　evaluationmethod ②由Cl作用破坏钢筋钝化膜;③由于SO4或其它 1　钢筋锈蚀机理及损坏特征 -2- 由于混凝土内埋置钢筋的锈蚀,混凝土开裂导 致的构件承载力不足引起的结构耐久年限降低这个问题,是影响混凝土结构耐久性的最主要因素之一。在工业厂房中,除化工车间、酸洗车间等有侵蚀性化学物质扩散的车间外,因钢筋锈蚀引起的结构耐久性破坏比较多见。在水工、海工及道桥结构中,钢筋锈蚀开裂破损的现象也很普遍。 在混凝土结构中钢筋锈蚀可以分为自然电化学腐蚀、杂散电流腐蚀、应力腐蚀及氢脆腐蚀。111　自然电化学腐蚀 当钢筋在强碱性环境中(pH值为1215～1312),表面会生成一层致密的薄膜呈钝化状态保护钢筋免受腐蚀。通常周围混凝土对钢筋的这种碱性保护作用在很长时间内也都是有效的。然而一旦钝化膜遭到破坏,钢筋就处于活化状态,就有受到腐蚀的可能性。 使钢筋的钝化膜破坏的主要因素有四点:①当无其它有害杂质时由于碳化作用破坏钢筋钝化膜; IndustrialConstruction2002,Vol132,No12 酸性介质侵蚀而使混凝土碱度降低钝化膜破坏;④混凝土中掺加大量活性混合材料或采用低碱度水泥,导致钝化膜破坏或根本不生成钝化膜。钢筋生锈的内部条件是钝化膜遭到破坏,产生活化点;钢筋锈蚀的外部条件是必须有水及氧的作用。当这几个条件同时存在时,则构件内部存在电位差,可以产生局部腐蚀电池,钢筋就会产生锈蚀。11112　几种典型的腐蚀特征 (1)在工业厂房中,对于侵蚀性介质较少的厂房(炼钢厂房、轧钢厂房),混凝土结构中钢筋锈蚀容易发生的部位一般位于屋面板及柱根处,这些部位构件容易受到水的浸淋、浸泡,经常处于潮湿状态,这些构件的锈蚀都是在混凝土碳化后发生,一般混凝土表面没有保护措施,锈蚀的特征通常是在屋面板大肋及柱角沿钢筋出现纵向裂缝。 (2)对于酸洗车间这些有酸性介质侵入的厂房 第一作者:惠云玲　女　1960年11月出生　教授级高级工程师收稿日期:2001-09-25 工业建筑　2002年第32卷第2期　　5 (相当于CEB2FIP规范中混凝土暴露等级5b、5c级 无关,当表面只有轻微损