粉煤灰对氯氧镁水泥作用和影响 　　摘要:通过对比试验研究了不同掺灰量对氯氧镁水泥强度、耐水性、体积稳定性的影响,得出粉煤灰最佳掺量。试验结果表明,粉煤灰是一种理想的添加剂,可使氯氧镁水泥制品的耐水性得到明显改善,提高体积稳定性而且对氯氧镁水泥制品的强度影响很小,并有利于后期强度的增长。 　　Abstract: By comparing the effects of different amount of lime and fly ash on the strength of magnesium oxychloride cement, water resistance, volume stability, the best mixture of fly ash cement is got. The results showed that fly ash is an ideal additive, and the using of magnesium oxychloride cement products have significantly improved water resistance and improve the stability and volume of magnesium oxychloride cement products on the strength of little effect, which contributes to the later growth. 　　关键词:粉煤灰;氯氧镁水泥;作用;影响 　　Key words: fly ash; magnesium oxychloride cement;function;influence 　　中图分类号:TU528文献标识码:A文章编号:1006-4311(2010)04-0240-02 　　 　　氯氧镁水泥,又称菱镁水泥、镁水泥、索瑞尔(Sorel)水泥,是用轻度煅烧菱镁矿(MgCO3)粉磨而成的轻烧氧化镁粉(MgO)和氯化镁溶液(卤水)调制而成的一种气硬性胶凝材料,其原料来源丰富,生产工艺简单,成本低,所得制品硬化快、强度高、表面光泽好,防火性能好,广泛用于制作防火板、防火门、玻璃纤维增强波瓦、代木包装材料、隔墙板、活动板房、农用大棚骨架、煤矿井下支架等。但是由于制品本身耐水性差严重阻碍了氯氧镁水泥的广泛应用,国内外学者提出了很多方法改善这种水泥的耐水性,本实验在这方面也作了大量的研究,结果发现粉煤灰就是一种很好的添加剂。 　　1原材料选择 　　(1)MgO辽宁大石桥, 活性MgO含量57%; 　　(2)卤块(MgCl2?6H2O)青海产,MgCl2含量为45%; 　　(3)粉煤灰辽宁阜新细度不应小于120目,材料干燥。 　　轻烧氧化镁粉和粉煤灰的主要化学成份如表1和表2所示。 　　表1氧化镁的化学成份(%) 　　表2粉煤灰主要化学成份(%) 　　2实验过程 　　为了说明不同龄期、不同掺量粉煤灰对氯氧镁水泥制品强度的影响,我们只考虑粉煤灰单一因素。 　　在MgO-MgCl2-H2O三元相图理论指导下,形成以5?1?8相为主要水化产物,确定实验的基本???比为MgO:MgCl2:H2O=7.9:1:14.6(摩尔比),粉煤灰的掺量0~40%。 　　具体方法为:称取轻烧菱镁粉,粉煤灰搅匀,在称取氯化镁,水(室温),放入烧杯充分搅匀。最后把所有的原料放入每分钟120转的搅拌锅搅拌6分钟,在搅拌期间掺入减水剂(占轻烧菱镁粉1%)。然后浇注入Φ40mm×40mm×160mm的钢模成型,1d后脱模,在室内分别养护3d、7d、28d后进行强度实验。 　　3结论及分析 　　图1氯氧镁水泥的28d以后的XRD图谱 　　(A:5?1?8相,B:MgO,C:Mg(OH)2,D:MgCO3,E:α-SiO2,F:莫来石,G:Mg2P2O7) 　　对粉煤灰预掺15%的试样进行XRD分析,其结果如图3.1所示。从图中可以看出氯氧镁水泥的水化产物主要由5?1?8相以及少量未分解的MgCO3、未反应的MgO、中间相α-SiO2和莫来石等组成的。衍射图中α-SiO2和莫来石的特征峰主要由内掺的大量粉煤灰引入硬化体系中而引起的。 　　3.1 粉煤灰对氯氧镁水泥强度的影响 　　图2、图3分别是不同龄期、不同掺量的粉煤灰对抗压强度和抗折强度的影响。不同配比、不同养护龄期实测强度值从上述结果可以看出,随着粉煤灰加入量的增加,氯氧镁水泥的强度呈现逐渐下降的趋势。 　　当粉煤灰掺量为5%时,氯氧镁水泥制品材料的抗压强度和抗折强度基本保持不变;当粉煤灰掺量为10%~25%时,氯氧镁水泥制品材料的抗压强度下降幅度为20%左右,但基本上保持稳定