TiOCFA复合材料制备及光催化性能研究 　　摘 要：以电厂废弃物粉煤灰作载体，钛酸丁酯为钛源，采用溶胶-凝胶法正交实验制备二氧化钛/粉煤灰（TiO2/CFA）复合材料，以亚甲基蓝为目标污染物，进行光催化处理，探究其最佳制备条件和影响因素。结果表明，TiO2/CFA最佳制备条件为负载率40%、焙烧温度500℃、焙烧时间0.5h，降解率可达到77.8%。通过极差分析可得，影响降解性能顺序为焙烧温度焙烧时间负载率。TiO2/CFA能够有效的去除废水中的亚甲基蓝，具有一定的实用价值。 中国论文网 /1/viewhtm 　　关键词：二氧化钛；粉煤灰；光催化；亚甲基蓝 　　中图分类号：X52 文献标识码：A 文章编号：2095-2945（2018）14-0032-03 　　Abstract： Titanium dioxide/coal fly ash（TiO2/CFA） composite was prepared by Sol-Gel Method using coal fly ash as carrier and butyl titanate as titanium source. Methylene blue was used as the target pollutant for photocatalytic treatment. The optimum preparation conditions and influencing factors were investigated. The results show that the optimum preparation conditions of TiO2/CFA are as follows： loading rate 40%， calcination temperature 500℃， calcination time 0.5h， and the degradation rate can reach 77.8%. Through the range analysis， the order of influencing degradation performance is calcination temperaturecalcination timeloading rate. TiO2/CFA can effectively remove methylene blue from wastewater， and has certain practical value. 　　Keywords： titanium dioxide （TiO2）； coal fly ash （CFA）； photocatalysis； methylene blue 　　TiO2等半??体光催化剂负载和掺杂是提高光催化剂性能的有效途径[1]。粉煤灰是燃煤电厂排放的固体废物，近年来采用粉煤灰负载TiO2降解水中有机物研究成为热点。Xuan等研究表明粉煤灰经过处理后可作为SCR催化剂载体[2]。段瑞斌等研究了粉煤灰负载TiO2的制备方法[3]，霍炜江等研究了硝酸化粉煤灰负载TiO2的制备及光催化性能[4-5]。然而目前研究多在于TiO2负载量对其光催化率影响，很少有涉及制备工艺因素对光催化剂制备及效能影响。 　　本研究采用溶胶-凝胶法制备纳米TiO2，并将其负载于粉煤灰上，以亚甲基蓝作为目标污染物[6-7]，采用正交实验探究TiO2负载量、焙烧温度、焙烧时间对亚甲基蓝光催化性能影响。制备的二氧化钛/粉煤灰（TiO2/CFA）复合材料为粉煤灰回收利用及水中有机污染物去除提供一种新途径。 　　1 材料与方法 　　1.1 实验材料与仪器 　　1.1.1 实验材料 　　选取宝鸡某发电厂的粉煤灰作为主要原料，主要试剂如表1所示。 　　1.1.2 实验仪器（见表2） 　　1.2 制备与检测方法 　　1.2.1 粉煤灰预处理 　　将粉煤灰过100目筛，经马弗炉700℃煅烧2h后降至室温，得到粉煤灰预处理样品。 　　1.2.2 纳米TiO2制备 　　采用溶胶-凝胶法制备纳米TiO2胶体[8-9]，首先取无水乙醇67mL放置在磁力搅拌机上以120r/min进行搅拌，边搅拌边缓慢加入17mL钛酸丁酯，滴加完后加入4.8mL二乙醇胺，搅拌30min，然后加入0.9mL去离子水，9mL无水乙醇及适量浓盐酸摇匀后倒入杯中，连续搅拌2h后静置得纳米二氧化钛胶体。 　　1.2.3 粉煤灰负载TiO2制备 　　采用混合泥浆制备方法，将预处理后的粉煤灰称取一定量放入坩埚中，向坩埚内滴加10mL TiO2胶体，搅拌使其混合均匀，放入烘箱中于105℃下烘干，放入马弗炉（已预热）50