无机聚合物钢纤维混凝土动态压缩性能试验分析-experimental analysis of dynamic compressive properties of inorganic polymer steel fiber reinforced concrete.docxVIP

武汉 武汉理工大学硕士学位论文 万方数据 万方数据 Abstract Inorganic polymer concrete as a new green building material, because of their low cost price, less environmental pollution, radiation resistance, good permeability and rapid hardening early strength and other characteristics, has been the concern of many scholars. However, inorganic polymer concrete（IPC）often showed great fragility in force process, usually by adding fiber to inorganic polymer concrete to improve its toughness. This article added steel fiber to inorganic polymer concrete to study the mechanical properties of the impact load, the main research work and achievements include the following aspects: Cube static compressive experimental study of inorganic polymers steel fiber reinforced concrete（IPSFRC） and IPC were proceed. Studies have shown that: IPSFRC is slightly higher than the intensity of IPC with respect to the latter by about 7%; On the failure patterns, IPC surface was peeling and had certain micro-cracks, however IPC flaking serious. Through the dynamic compression tests on the split Hopkinson pressure bar (SHPB) device of IPSFRC, IPC as well as ordinary steel fiber reinforced concrete （SFRC）, getting three kinds of materials under different strain rates of stress - strain curves, and organize by the failure patterns of the material at different strain rates. From the main mechanical parameters of failure stress, peak strain, peak toughness analysis the influence of strain rate to dynamic compression IPSFRC. With the increase of strain rate, failure stress, peak strain, peak toughness of inorganic polymers steel fiber reinforced concrete also will increase the peak strain, clearly reflected sensitive for strain rate. In terms of the dynamic compressive mechanical properties, IPSFRC is significantly better than IPC. The dynamic material properties of IPSFRC and SFRC with the same content of steel fiber are compared with each other peak, The result shows that the dynamic strength and toughness of IPSFRC i