原油稳定塔拆除过程中防止FeS自燃施工措施.docVIP

原油稳定塔拆除过程中防止FeS自燃施工措施 　　【摘 要】本文探讨了FeS生成及FeS与空气中的氧气结合而发生自燃、爆炸的机理。简述了原油稳定塔拆除过程中,为防止FeS自燃现象的发生,保证拆除工作安全、顺利的开展,而制定的施工措施。 　　【关键词】 FeS;自燃;爆炸 　　Construction measures to prevent spontaneous combustion of FeS during crude oil stability tower removal process 　　Liu Jun, Huang Wei-an, Zhang Chang-sheng 　　(Jiangsu Petroleum Exploration Bureau Oilfield Construction Department Jiangdu Jiangsu 225261) 　　【Abstract】This article discusses the FeS and FeS formation and combination of oxygen in the air would ignite the explosion mechanism. Stability of crude oil briefly tower demolition process, in order to prevent spontaneous combustion phenomena FeS, to ensure removal of the safety and smooth conduct, and the development of construction measures. 　　【Key words】FeS; Spontaneous combustion; Explosion 　　1. 前言 　　江苏油田富民联合站初建于80年代,该站经过多次改造扩建,主要以原油稳定、油气水分离、注水及污水处理为主。目前根据富民油区产能需要进行调整,将站内停用多年的原油稳定区设备、容器及管网进行拆除。拆除工作量主要涉及原油稳定塔、加热炉、电脱水器、浮头换热器、混烃罐、轻油罐、三相分离器等容器共十台,同时拆除设备容器间的管网。在这些设备容器中,仍然残存有一定量原油和天然气。 　　2008年夏天,该站一台三相分离器在开罐作业时,意外发生爆炸,后经专家鉴定是硫化亚铁自燃引起。 　　江苏油建安装一公司承担原油稳定区设备和管网的拆除任务,面对拆装过程中可能发生硫化亚铁自燃甚至爆炸的风险,经过多次论证制定了周密的施工措施。 　　要防止硫化亚铁自燃现象的发生,首先要了解硫化亚铁的产生和发生自燃现象的机理。 　　2. 硫化亚铁的产生、自燃机理及分布规律 　　2.1 硫化亚铁产生的机理 　　油品中的硫大致分成活性硫和非活性流两大类。活性硫包括单质活性流(S)、硫化氢(H2S)、硫醇(RCH2CH2SH),其特点是在一定温度下与铁反应生成硫化亚铁。 　　Fe+S=FeS 　　H2S+Fe== FeS+H2 　　RCH2CH2SH+Fe==RCHCH2+FeS+H2 　　2.2 硫化亚铁自燃的机理。 　　FeS是深棕色或黑色固体,难溶于水,密度4.74g/cm3,熔点1193℃。目前的原油处理都采用密闭的工艺流程,即使含有硫化亚铁,也不可能发生自燃现象。硫化亚铁在空气中受热或光照时,与氧发生如下化学反应: 　　FeS+3/2 O2=FeO+SO2+49KJ 　　该反应过程中,负二价硫氧化成四价硫,放出一定热量。由于氧化亚铁(FeO)在空气中不稳定,继续发生下列反应: 　　2FeO+1/2 O2=Fe??2O3+271KJ 　　硫化亚铁与氧气发生反应时,二价铁离子被氧化成三价铁离子放出更大量的热量。由于局部温度急剧升高,在比较密闭的容器中,当其中存在可燃的油或气时,会迅速燃烧,以致发生爆炸事故。 　　2.3 FeS在原油处理设备中的分布规律。 　　FeS在原油处理设备中的分布一般遵循这一规律:原油中硫含量越高,产生FeS越多;微细的FeS产物会随油品从上游不断地往下游转移;在油品流动速度相对较低的区域,不断地聚集沉积下来,因此在容器底部就会有更多的硫化亚铁聚集沉积。 　　3. 原油稳定塔拆除过程中防止FeS自燃的施工措施 　　原油稳定装置拆除过程中,为预防FeS自燃现象发生,最重要一环就是不能随意开启设备容器的人孔、手孔、清扫孔及阀门等,防止空气进入设备体内,严格控制设备体内的氧气含量。 　　这十台需拆除的设备中,原油稳定塔的体积、重量及高度最大,其外形尺寸为??1m×21m,整体总重量约为18吨。下面重点阐述原油稳定塔的拆除方案: