浅谈沥青混合料有效压实时间重要性 　　摘要：通过对西商高速35标沥青面层施工有关实测数据的分析，探讨了面层厚度（摊铺厚度），碾压温度，风力，气温（下承层温度），太阳辐射等因素对沥青混合料有效压实时间的影响，得出面层厚度和初压温度对沥青混合料有效压实时间有重要影响的结论，且分别符合指数函数关系和对数函数关系，对沥青面层施工有指导意义。 　　关键词：沥青混合料；有效压实时间 　　Abstract: Through to the west to high speed 35 standard of asphalt surface on the analysis of the measured data, discussed the thickness of the surface layer ( paving thickness ), rolling temperature, wind, temperature ( temperature of the under layer ), solar radiation and other factors on the time available for asphalt mixture compaction effect, that the thickness of the surface layer and the initial pressure temperature on asphalt mixture effective compaction time has important implications for the conclusion, and were consistent with exponential function and logarithmic function, the asphalt layer construction has guiding significance. 　　Key words: asphalt mixture; effective compaction time 　　?ぶ型挤掷嗪牛?U415文献标识码：A 　　 　　1、前言 　　良好的沥青路面质量最终要通过碾压来体现，如果碾压中出现任何质量缺陷，必将前功尽弃，因此必须重视碾压工作，并从提高实压度的角度对碾压作业进行了较全面和较深入的研究.随着沥青路面的大规模铺筑，我国也进行了类似的研究。由于材料来源、施工工艺、气候与环境条件的不同，本文结合来自西商高速35标面层施工的数据，探讨了气候、风速、面层厚度、碾压温度、太阳辐射等因素对沥青混合料有效压实时间的影响规律，以期能在生产中推广应用，从而提高沥青混合料的压实质量和沥青路面的使用品质和寿命。 　　 2、沥青面层施工概况 　　西商高速35标沥青混凝土路面工程由中交二公局施工。其面层结构为：12cm粗粒式沥青混凝土+5cm中粒式沥青混凝土，下承层为二灰碎石。 　　3、试验检测观测方案 　　压实质量与压实温度有直接关系，而摊铺后混合料温度是在不断变化的，因此必须掌握好有效压实时间，适时碾压。所谓有效压实时间是指：混合料从摊铺后的温度，降至最低允许碾压温度所需的时间。根据经验和相关文献介绍可知，可用于压实的有效时间主要取决于气温、下承层温度、太阳辐射、风速、摊铺厚度、初压温度等因素。 　　观测方案的选择原则是观测量最小且能满足研究分析问题的需要。通过按照乘法原则、正交设计和人为干涉法三种方案观测的计算及综合筛析，最后采用人为干涉法设计观测方案（见表2）。 　　表2 观测方案设计表 　　 　　 　　 　　 　　表中风力是根据当日的天气预报结果并结合工地实际情况而确定的；由于缺乏观测现场的标准太阳辐射值，估仅以天气阴晴来粗略表示太阳辐射的强弱；因气温与下承层温度存在一定对应关系，故没有单独考虑下承层温度对有效压实时间的影响；气温和沥青混合料温度是采用温度计测量的实测值，并在面层中部测量沥青混合料温度。我国《公路沥青路面施工技术规范》（JTJ F40--2004）规定当终压压路机采用刚轮、轮胎、震动压路机时，其分别对应的碾压终了温度为70度、80度、70度。而美国的试验表明，当沥青混合料的温度低于90度时，碾压实际上已不再明显增加沥青混凝土的密实度。因此，结合工地实际情况确定以沥青混合料温度下降至80度的时间为有效压实时间。 　　4、试验实测数据的处理与分析 　　 (1)气温、摊铺温度和初压温度 　　在不同条件下的沥青混合料有效压实时间见表2，对A组实测数据进行回归分析（见图1），发现曲线均为对数函数形式，回归如下。 　　T=T0-mlnt(1) 　　 式中：T为初压开始后时间t时的沥青混合料温度(℃