自流平砂浆配合比研究和强度预测.docVIP

自流平砂浆配合比研究和强度预测 　　【摘 要】应用普通硅酸盐42.5R水泥和天然河砂（细度模数为2.9）、复合外加剂及Ⅰ级粉煤灰制备了大流动性、高强度的自流平砂浆。应用水胶比、灰胶比和胶砂比三个不同层次的填充因素进行配合比的正交设计，确定了自流平砂浆的最佳配合比。对强度、内聚力的关系进行回归分析，推出了自流平砂浆7天和28天的强度计算公式。 　　【关键词】自流平砂浆；配合比；强度；内聚力；预测 　　 　　Research on the mix Proportion and Strength Prediction of Self-leveling Mortar 　　Li Dong-yan 　　(Qinhuangdao leading Qin administration bureau Qinhuangdao Hebei 066001) 　　【Abstract】 In this paper, the silicate 42.5R cement, river sand (Mx=2.9), composed admixture and fly ash was used to prepare big mobility ,high-strength self-leveling mortar. The three factors, water-binder ratio, cement-binder ratio and binder-sand ratio were used in crossing experiment to mix design. On basis of this, the best mix proportion of self-leveling mortar was decided. The adhesiveness and strength was analyzed through linear regression which based on lucubrate to cohesion force and adhesiveness. As a result, strength calculation formulas for 7 days and 28 days were put forward and strength forecast come to realization. 　　【Key words】Self-leveling mortar; Of friction; Strength; Mix proportion; Cohesion force;Prediction 　　 　　1. 前言 　　 　　1977年国内首批高强灌浆料CGM研制成功［1］以来，经过20多年的研究实践，我国灌浆料的技术性能逐步提高，尤其是外加剂的问世和使用，更加速了灌浆料的发展，各种性能和用途的灌浆料不断研制出来，有些灌浆料的各项技术性能指标已达到国际水平。在灌浆料的使用上，已从传统的用于机械设备安装的二次灌浆，发展到用于混凝土结构的加固修补，基础加固，建筑物植筋，梁、板、柱改造［2］、预应力孔的灌浆和梁板钢筋高密度密集区的灌浆［3］等多种用途，并取得了良好的效果。 　　目前，国内高强灌浆料一般多采用特种胶结材料和高强骨料配置（如CGM灌浆料），特种胶凝材料具有强度高、早强快硬、微膨胀等特点，高强骨料具有棱角，与水泥粘结性好，含泥少。但是特种胶凝材料因产源少、存期短、价格高，应用受到很大限制。因此国内有些学者已开始研究应用其他材料来配制，例如用特细砂加石屑［4］，明矾加石膏［5］，LNC高强灌浆料［6］等来研制，所用材料依然有一定限制。如果能用与普通砂浆相同的原材料，掺加外加剂和掺合料，通过配合比设计而配制出具有高流动性、高强度灌浆材料，无疑具有重大的实际意义。 　　 　　2. 实验研究 　　 　　2.1 实验原材料 　　（1）水泥:选用秦皇岛产42.5R型普通硅酸盐水泥。该水泥的各性能指标见表1。 　　（2）骨料:采用级配良好、细度模数为2.9的河砂，并用5mm过筛，含泥量小于2%。 　　（3）粉煤灰: 选用了天津热电厂生产的Ⅰ级粉煤灰，其各项技术性能见表2。 　　 （4）外加剂：制备自流平砂浆的外加剂有减水剂、缓凝剂、引气剂、收缩补偿剂见表3。 　　 　　2.2 试验方法 　　2.2.1 最佳掺量的确定。应用水泥净浆流动度试验方法，对外加剂和粉煤灰进行水泥适应性试验。确定了它们的适宜掺量，见表3。 　　2.2.2 自流平砂浆配合比试验正交设计。确定了复合外加剂（减水剂、引气剂、缓凝剂和收缩补偿剂）的用量和粉煤灰用量的合理范围。根据砂浆试配结果，确定本组实验采用正交表L9(33)，