浅述南水北调大断面倒虹吸混凝土裂缝处理技术.docVIP

浅述南水北调大断面倒虹吸混凝土裂缝处理技术 　　摘 要大断面混凝土表面产生裂缝的原因复杂而繁多主要由于混凝土在硬化时，由混凝土内部温度与外界的温差过大产生约束力，从而产生裂缝。采用“环氧树脂”胶凝材料对裂缝进行化学灌浆处理，能够使构筑物的开裂面达到“防渗补强”的目的，取得了较好的内在质量和外观效果。 　　关键词南水北调； 大断面；倒虹吸； 裂缝处理 　　Abstract: There has variety of causes for the cracks in the surface of large section concrete, and the major is that in the hardening, the excessive temperature difference between the interior and exterior of concrete produces constraint force, which causes the cracks. The epoxy resin cementitious material applied to process the chemical grouting can prevent the seekage and reinforce of the cracks of buildings, so as to achieve favorable internal quality and exterior effect. 　　Key words: the South-to-North Water Diversion Project; large section;inverted siphon; crack processing 　　中图分类号： TU377文献标识码：A文章编号：2095-2104（2012） 　　 　　1工程概况 　　南水北调中线工程河渠交叉建筑物沧河渠道倒虹吸，总长度849m，倒虹吸管身横断面为3孔一联箱型钢筋混凝土结构，单孔净空尺寸为6.8m×6.8m（高×宽）。结构设计厚度：底板为1.2m，顶板为1.2m，边墙为1.2m，中墙为1.1m，单节长度14.5m。 　　2混凝土开裂情况简述 　　倒虹吸管身混凝土，采用大型液压布料机及大型钢模台车浇筑的方法施工，单仓最大浇筑方量为1500m3，属于大体积混凝土。底板混凝土浇筑脱模第3~43天后检查发现，部分边、中墙基本墙体的中间部位，产生了高度为2 m ~4m，缝宽为0.02mm~0.3mm的裂缝，裂缝倾角与地平面呈80°~90°，走向与水流方向基本垂直，开裂走向与倾角呈现规律性。经压水和超声波检测，一部分为半缝，一部分为贯通缝。 　　裂缝产生后，业主、设计、、监理、施工等多家单位的专家、教授，召开裂缝成因分析和处理专题研讨会，最终确定采用“防渗补强，外表美观”的裂缝处理原则。依据《水工建筑物化学灌浆施工规范》DL/T5046-2010，参照国内同类工程经验，编制施工方案和技术措施，开展裂缝处理技术研究。 　　3施工准备工作 　　3.1施工设备配置 　　施工设备配置表 　　 　　3.2注浆材料 　　 (1)胶凝材料 　　选用德聚牌“混凝土裂缝处理环氧树脂灌浆料”，由主剂和固化剂双组份组成。 　　 (2)封缝材料 　　选用聚脂胶碳纤维布。 　　 (3)灌浆嘴 　　选用裂缝处理化学灌浆专用产品。 　　4工艺流程 　　钻灌浆孔→清洁灌浆孔→清洁聚脂胶与混凝土结合面→黏贴封缝聚脂胶碳纤维布→安装灌浆嘴→封缝布待强→灌注浆液→浆液待强→质量检测→外观处理。 　　5化灌处理的工艺方法 　　5.1钻孔 　　 ⑴ 采用“钻孔灌注法”进行化学灌浆，依据《水工建筑物化学灌浆施工规范》“采用钻孔注浆法时，钻孔可布置在裂缝的一侧或两侧。斜孔孔径不小于12mm”的要求，钻孔形式采用斜向孔的方式进行，选用参数为：手电钻钻头直径为∮14mm，钻孔沿裂缝两侧各10cm～12cm布置，钻孔斜度45°～50°，孔距20cm～25cm，梅花型孔位。切实保证注浆孔与裂缝之间的通畅性和浆液的可灌度。 　　⑵钻孔如遇到钢筋立即停止，移动孔位，必须保证受力筋、构造筋不被破坏。 　　⑶采用自下而上注浆顺序，注浆孔上部每隔一个孔（孔距40cm～50cm）不装注浆嘴，以替代排气孔和注浆饱满度检查孔。 　　5.2清孔及混凝土与封闭布结合面清洁 　　 ⑴清孔 　　采用0.7MPa的高压风，将∮10mm软塑管插入接近孔底，由内向外，分段将孔内粉尘吹出，保证孔内清洁。 　　 ⑵混凝土与封闭布结合面清洁 　　封缝前，要将聚脂胶碳纤维布与混凝土结合面的乳皮、污染物打磨清理，用高压风吹