pdc陶瓷基无线无源温度传感器的制备与测试材料工程专业论文.docxVIP

AbstractAbstract Abstract Abstract Hi曲temperature and corrosive gas environment is the main feature inside the gas turbine．However,developing such a kind of sensors is a huge technical challenge since the sensors must survive the hi【gh temperature，as well as corrosive gas，both structurally and functionally．PDC has excellent high temperature resistance，and is particularly suitable for being used in hi曲temperature environment．The passive wireless temperature sensor used PDC as sensing element is expected to realize real-time temperature monitoring inside the gas turbine． DP is used as the thermal crosslinking agent．PVSZ is used as preceramic of PDC—SiCN．PBSZ is used as preceramic of PDC-SiBCN．PVSZ and ASB are used as preeeramic of PDC-SiAlCN．PDC—SiCN，PDC-SiBCN and PDC-SiAlCN are prepared，respectively．Hi曲temperature dielectric property testig shows that谢Ⅱ1 temperature increasing，the dielectric constants of PDC-SiCN and PDC-SiAlCN are increased．High frequency dielectric property testing shows that after free-carbon oxy·genated，the dielectric constant and dielectric loss of the PDC-SiAlCN are all reduced along、Ⅳi也the aluminum content of PDC-SiAICN increased． Under the same testing temperature，the study of wireless passive temperature sensor used PDC—SiCN with different diameter as sensing elements and silver and platinum as cavity materials shows that the resonant frequency of the sensor are increased when the diameter of PDC-SiCN decreased．And the highest testing temperature of the PDC-SiCN based wireless passive temperature sensors is 800℃， 、衍m the corresponding sensitivity and resonant frequency are 1 0．3 8 GHz and 0．543 7 MHz／℃．The study of wireless passive temperature sensor used PDC-SiBCN pyrolyzed in different temperature as sensing elements and silver and platinum as cavity materials shows that for the the sensor made of the PDC-SiBCN pyrolyzed in 1 000～1 200℃，the resonant frequency of the sensor is decreased when the pyrolyzed temperature of PDC-SiBCN increas