1018油气田地面工程新技术培训班-郑树启-天然气管道的腐蚀与防护技术.ppt

* H2S 环境中金属抗硫化物应力开裂和应力腐蚀开裂的室内试验 NACE Standard TM0177-2005 Item No.21212 * * 酸性油气田耐蚀合金抗应力腐蚀开裂评价的慢速率拉伸试验方法Slow Strain Rate Test Method for Screening Corrosion-Resistant Alloys (CRAs) for Stress Corrosion Cracking in Sour Oilfield Service NACE Standard TM0198-1998 * * * * * * Today we are going to be talking about the basic of tire construction and a few basic about the theory of the tire. we will be looking at what a tire is made of because we know that it can just be rubber because it is black. So we will actually show you what percent of a tire actually is rubber and is it really black because it is made of rubber. * * * * * 母材 细晶区 粗晶区 焊缝 * 控制焊接区域维氏硬度 * 合金元素的影响 有害元素：Ni、Mn、S、P; 有利元素：Cr、Ti Ni：即使其硬度HRC＜22时, 也不应该超过1％。含镍钢之所以有较大的应力腐蚀开裂倾向，是因为镍对阴极过程的进行有较大的影响。在含镍钢中可以观察到最低的阴极过电位，其结果是钢对氢的吸留作用加强,导致金属应力腐蚀开裂的倾向性提高。 * 1%Ni含量碳钢，SSC敏感严重 * 控制硬度250HV（22HRC），Q+T C90和T95油套管可以270HV 硬度偏差10%以内 确保没有未回火马氏体 N80和C95可用于65℃以上工况，高于℃ C95、N-80、 P105和 P110可用，高于110 ℃，Q125可用 冷变形后必须620 ℃以上回火 无缝管的S含量不能大于0.01%，对铸件没有S含量要求，对于锻件S含量不能大于0.025% 热轧材料要控制夹杂形态、碳硫磷锰等含量、带状珠光体 * 防止钢的硫化氢腐蚀开裂的最有效最便宜的方法之一是采用缓蚀剂(链接）。缓蚀剂的作用在于它能吸附在金属表面，并形成单分子膜。新组成的缓蚀剂分子层可抑止腐蚀反应的进行，阻碍氢向钢中扩散(抑止质子放电阶段并使氢原子重组成氢的阶段易于近行)。 许多缓蚀剂在相当长的时间内都有保护作用，因此可以过间隔一定的时间将其加到钢的工作表面上。 目前使用的以及新研制的缓蚀剂，除了防护钢不产生疏化物腐力开裂外，还能防止钢的全面腐蚀。 * Corrosion2007-07659 * 20Cr-50Ni- 10Mo 25Cr-50Ni-6Mo 22Cr-42Ni-3Mo 25Cr-35Ni-3Mo 25Cr-30Ni 25Cr-7Ni 22Cr-5Ni Cr-Mn低合金钢 L80 * * 内 容 H2S腐蚀的基础知识 集输系统常见的腐蚀类型及特征 高酸性环境中碳钢腐蚀特征 元素硫腐蚀特征 非金属材料腐蚀特征 测试方法 * 元素S沉积对腐蚀速率、应力腐蚀的影响 * P203－1井加热炉出口的直管段 * * 硫单质对碳钢腐蚀的规律 宏观形貌 　 　30℃ 50℃　 90℃ 　腐蚀产物宏观形貌 　 　 　 　 　 去除腐蚀产物后试样基体宏观形貌　 　 　 x52试样表面宏观照片 * * * 温度对碳钢腐蚀规律研究 宏观形貌 　 　p110 　l360 　 　腐蚀产物宏观形貌 去除腐蚀产物后基体宏观形貌　 　腐蚀产物宏观形貌 去除腐蚀产物后基体宏观形貌　 　30℃ 　 　 　 　 　50℃ 　 　 　 　 90℃　 　 　 　 　 * H2S /CO2压力对碳钢腐蚀的影响规律 * 内 容 H2S腐蚀的基础知识 集输系统常见的腐蚀类型及特征 高酸性环境中碳钢腐蚀特征 元素硫腐蚀特征 非金属材料腐蚀特征 测试方法 * 集输系统中阀门、盲板中的密封件 * 腐蚀前 100℃ 121℃ 140℃ 150℃ 175℃ NACE标准实验橡胶在不同温度条件下腐蚀结果 橡胶高温高压H2S腐蚀 * 电线电缆140度 H2S腐蚀后照片 电线电缆100度 H2S腐蚀后照片 电线电缆失效实例 * 腐蚀前 100℃ 140℃ 121℃ 150℃ 175℃ 橡胶在