PAGE PAGE 1 7.8 溶剂型防涂鸦耐污涂料的制备 □ 周荣华 （深圳市天健集团（股份）有限公司，广东深圳 518122） 摘要：研究了一种以羟基丙烯酸树脂和改性聚二甲基硅氧烷树脂作为成膜物质，同时加入流平剂、消泡剂、催干剂、附着力促进剂等各种助剂和溶剂混合成的涂料，其与异氰酸酯固化剂交联常温自干成膜，具有优异的防涂鸦耐污性、耐黄变性、耐溶剂性、耐酸碱性、高密着性、施工方便等特点。 关键词：防涂鸦；耐沾污；聚氨酯涂料；溶剂型防涂鸦涂料 中图分类号：TQ630.7+9 文献标识码：A 文章编号：1006-2556(2008)09-0035-03 Preparation of solvent-borne anti-doodling contamination-resistance coatings Zhou Ronghua (Shenzhen Tonge(Group)Co., Ltd., Shenzhen 518122,Guangdong Abstract: Using hydroxyl acrylic resin and modified dimethyl silicone as binders, together with leveling agent, defoaming agent, drying catalyst, adhesion promoter and solvent, we have prepared the coatings, which can crosslink with isocyanate to dry at room temperature. They are of perfect anti-doodling contamination-resistance, anti-yellowing, solvent resistance, acid and alkali resistance, high adherence and convenient application. Keywords: anti-doodling, contamination-resistance, PU coatings, solvent-borne anti-doodling coatings 0 前言 涂鸦小广告被称为“城市牛皮癣”，会对市容市貌造成不良的影响，本文介绍了以丙烯酸树脂、硅氧烷树脂作为成膜物质的溶剂型防涂鸦耐污涂料的制备。试验结果显示这种涂料不仅可使涂鸦难以进行，而且施工方便，涂膜具有十分优异的耐候性、耐腐蚀性和高硬度、高密着性等性能。可应用于不锈钢、铁材、铝合金、玻璃等各种底材的设施上，具有广泛的应用前景。 1 试验部分 1．1 工艺原理 目前关于涂料耐沾污性的原理很多，大都涉及到涂料本身的性质，如漆膜的表面能、亲水/亲油特性、平整度、表面硬度、玻璃化温度等。防涂鸦耐污涂料主要是基于低表面能憎水特性的耐沾污机理，如果漆膜的表面能低于污染物，理论上污染物就很难稳定吸附在漆膜表面。防涂鸦涂料通过加入低表面能的改性聚二甲基硅氧烷树脂与固化剂中的－NCO组分反应固化成膜后，可得到耐沾污性很强的涂膜。 1．2 主要原料（见表1） 表1 原料及厂家/产地 名称 型号 厂家/产地 羟基丙烯酸树脂 306 源长 改性聚二甲基硅氧烷树脂 Protect 5000 佳旭 流平剂 BYK-358 BYK 消泡剂 5500 德谦 催干剂 DBTDL 帕斯托 附着力促进剂 AMEO 佳旭 附着力促进剂 650 重凯 附着力促进剂 6007 号东 附着力促进剂 AHP-100 增城惠登 固化剂 HTC-1990BA 轩羽 二甲苯 XYL 江海天 醋酸丁酯 BAC 江海天 1．3 溶剂型防涂鸦漆的配制 1．3．1 A组分的配制 配料时，先将Protect 5000加入到306树脂中，搅拌均匀后依次加入流平剂、消泡剂、催干剂、附着力促进剂、溶剂，用高速搅拌机搅拌，混合均匀即可。 表2 防涂鸦涂料配方设计 原材料品种 ω/％ 羟基丙烯酸树脂 90.0 改性聚二甲基硅氧烷树脂 1.0 流平剂 0.5 消泡剂 0.1 催干剂 0.05 附着力促进剂 1.0 二甲苯 7.35 1．3．2 B组分的配制（见表3） 溶剂型防涂鸦耐污涂料是由含羟基树脂与异氰酸酯固化剂交联反应而成，