青铜系代替铜鉄系烧结含油轴受-NTN.pdf

NTN TECHNICAL REVIEW No.82 （2014） [ 製品紹介 ] 青銅系代替銅鉄系焼結含油軸受 The Copper Iron-based Material Sintered Oil-impregnated Bearing Equivalent to Bronze Sintered Material 山 下 智 典* Tomonori YAMASHITA 一般に焼結含油軸受の材質は，青銅系，銅鉄系，鉄系に分類されている．青銅系材料はしゅ う動性，音響特性に優れているが，銅粉は鉄粉に比べると高価なため，使用量の抑制が課題 であった．今回,特殊な銅粉により，銅が少量でも青銅系材料と同等以上のしゅう動特性とな る材料を開発した．本稿では開発材料を用いた焼結含油軸受について紹介する． The materials of the sintered oil-impregnated bearing are classified into bronze-based, copper iron-based and iron-based in general. Bronze based materials are superior in sliding an acoustic feature, the problem is th copper powder is high cost compared with iron powder, so it was necessary to reduce its quantity. By adopting special copper powder, we developed new materials having same or surpassing sliding and acoustic features as in the existing bronze-based materials, even with the small amount of copper inside. This report introduces th sintered oil-impregnated bearing using developed materials. 1. はじめに 3. 特殊銅粉の特徴 焼結含油軸受は自動車や産業機械に広く使用されて 開発品の材料配合を表1に示し，この材料配合に基 おり，その材料は青銅系と鉄系および両者を組み合わ づき，特殊銅粉を用いた軸受の断面を図1に示す．図 せた銅鉄系に大別される．パワーウィンドやファンモ の上側が軸受内径面であり，表層に銅の薄層が形成さ ータなどの自動車電装品や，複写機やレーザービーム れている．特殊銅粉は，圧粉体表面部に集中する性質 プリンタなど，軸受に高いしゅう動性能が求められる があり，めっきなどの特殊工程を追加することなく， 用途に対しては，青銅系材料が適している．しかし， 通常の成形工程で，圧粉体が製作できる．一方，圧粉 近年の銅価格の上昇から，NTNは青銅系に代わる焼結 体内部には，材料混合時に配合した汎用の銅粉や鉄粉 軸受の新しい材料を開発した．本稿では，この青銅系 が多く含まれる． 代替銅鉄系焼結含油軸受の特性について紹介する． 図2に軸受内径面を示す．内径面の約60%以上は 銅が露出しており，これが優れたしゅう動性に寄与す