高分子表征技术 - 高分子结晶.pptVIP

The Crystal Structures: Nematic (N) 160 - 300 oC a Tm 160 oC orthorhombic a 2.56 nm, b 2.34 nm, c 3.32 nm a’ Tm 160 oC orthorhombic b 2.38 nm b phase Induced by solvent Chen, SH. et al., Macromolecules, ASAP. The Thermal Property: Crystal Structures from both Nematic and Isotropic Phases Crystal Growth from both Nematic and Isotropic Phases Crystallization from nematic phase Tc=135 oC 1 mm Crystallization from nematic phase Tc=145 oC Observation the Crystal growth 1 mm 2 mm 1 mm Tc=140 oC The influence on the Crystal growth direction Tc=140 oC 1 mm Tc=140 oC 1 mm Crystal Growth from Amorphous Phase The kinetic of crystal growth and controlling the growth direction 思考题 请推导Avrami方程，并指出各个系数代表的物理意义。 温度对球晶及片晶分叉有什么影响？为什么？ 环带球晶中片晶的扭转与螺位错的关系？ 熔体中高分子链的预取向对结晶有何影响？ 谢 谢！ 1μm In-situ twisting of the lamellae at 85°C Quenching to 35°C and Lamellar Branching 15μm 35°C phase 30μm height 30μm 30μm height phase Controlling the lamellar branching 片晶的生长 a b c e 400 nm 片晶生长的前端 Strobl, G Europ.Phys.J. E 2000, 3, 165. 1 2 3 400 nm 4 d c b 2 3 4 4 1 片晶前端缺陷的证据 a c e b 0.2 mm b 2 mm d 2 mm Asp/Ao ~ 0.7 ~ 0.6 ~ 0.44 球晶的形成 Formation of A Lamellar Sheaf a 500 nm b 1 mm c 1 mm Height Phase 球晶和片晶与温度的关系 35°C 45°C 55°C 15μm 15μm 15μm 1μm 1μm 1μm height phase 球晶和片晶与温度的关系 65°C 75°C 2μm 15μm 20μm 20μm 2μm 1μm height phase 球晶和片晶与温度的关系 20μm 1μm 2μm 2μm 2μm 40μm 100μm 80°C height phase 片晶与温度的关系 100μm 100μm 100μm 100μm 100μm 100μm 85°C height 是由于折叠表面与高分子链段不垂直，导致片晶上下表面积累不对称的应力造成的，取决于片晶内的原因； 因为形成与片晶生长同方向的螺旋位错，导致片晶的扭转，属于片晶外部的原因。 100μm 100μm 2μm 1μm 60°C 60°C 90°C 90°C phase phase height 螺旋位错 链倾斜 静态研究不能解决问题！ 片晶扭转现象的争议 环带球晶的片晶结构 2 mm 400 nm 环带球晶的片晶结构 100μm 100μm 2μm 1μm 60°C 60°C 90°C 90°C phase phase height 原位研究环带球晶中片晶的扭转（25 oC） 5μm 1μm 5μm 1μm 1μm 1μm phase height phase phase phase phase 原位研究环带球晶中片晶的扭转（75 oC） 3μm phase 原位研究环带球晶中片晶的扭转（85 oC） 1μm phase 片晶扭转机理和模型 Twisted crystal growth before screw dislocati