特厚板品种生产现状及新技术研究.docxVIP

特厚板品种生产现状及新技术研究刘清梅 魏丽艳( 首钢技术研究院，北京 特厚板品种生产现状及新技术研究 刘清梅 魏丽艳 ( 首钢技术研究院，北京 100041) 【摘要】 特厚板品种生产现状为开发高性能产品。阐述了特厚板产品生产现状以及品种 使用性能的要求。分析了新加速冷却技术、在线热处理技术、钢锭单向凝固技术和焊接复合技 术在特厚板品种开发中的作用。新技术的应用推进了特厚板品种开发的高效性和实用性。 【关键词】 特厚板 加速冷却 热处理 单向凝固 焊接复合 MANUFACTURING STATUS OF SPECIAL HEAVY-THICKNESS PLATE GRADES AND THE STUDY OF NEW TECHNIQUE Liu Qingmei Wei Liyan ( Shougang Research Institute of Technology) 【Abstract 】 Manufacturing status of special heavy-thickness plates was to develop the high performances products． The manufacturing status of special heavy-thickness plate productions and operating requirements were represented． Furthermore，the role of super on-line accelerated cooling technique，heat treatment on-line process，unidirectional solidification of ingot steel and welding compound technique in the special heavy-thickness plate grades exploitation were analyzed． The application of new technique impelled the high efficiency and practicability of the exploitation of special heavy-thickness plate grades． 【Key Words】 Special Heavy-Thickness Plate，Accelerated Cooling，Heat Treatment，Unidirec- tional Solidification，Welding Compound Technique 随着我国基础结构建设项目的不断增加，对 特厚钢板的市场需求量越来越大。为提高特厚板 的使用安全性，对特厚板的强度要求越来越高，同 时还要求特厚板具有较低的屈强比、较高的低温 韧性、良好的抗层状撕裂性能和焊接性能［1］。为 了达到特厚板的各项性能指标，新的特厚板生产 技术开发已经成为世界各大钢铁企业高度重视的 问题。本文就目前特厚板系列品种生产状况及特 厚板生产的新技术做详细的分析。 产品。 1． 1 海洋工程装备用特厚板系列产品开发 海洋工程装备用特厚板主要有海洋平台和海 洋风力发电用特厚板。其中，海洋平台用特厚板 由于在海洋上特殊场所进行作业，所以必须具有 高强度、高韧性、抗疲劳、抗层状撕裂、良好的焊接 性及耐海水腐蚀等。海洋风力发电用特厚板由于 要经受风、浪、流、地震等灾害性环境的考验，所以 对结构防腐、高应力区结构型式以及焊接工艺等 有高要 求。目前国际海洋平台用钢主要级别为 355、420 MPa 和 460MPa［2-3］，比如 355 级 En10225 的 S355、420 级 En10225 的 S420、460 级 En10225 的 S460。我国生产了 EH36 以下平台用特厚板和 1 特厚板系列品种开发状况 根据企业的发展和市场需求，特厚板系列品 种开发比例逐年增大，高强度、高等级、高技术含 量和高附加值品种的特厚板逐渐成为钢厂的主打 作者简介: 刘清梅，女，博士，从事特厚板品种开发炼钢工艺研究 58上 海金属第 33 卷厚度在 150 mm 以上的 A517Q 58 上 海 金 属 第 33 卷 厚度在 150 mm 以上的 A517Q 海洋石油平台用齿 条钢等［4］，但关键部位所用大厚度、高 强 度 钢 材 仍依赖进口。 的条件下，随着冷却的进行，温度的偏差会不断增 大，引起板表面不均匀冷却，恶化了钢板的质量。 为了解决这个问题，在热轧后经特殊设计的加速 冷却技术