不同导热系数的挤塑板燃烧性能研究.docxVIP

不同导热系数的挤塑板燃烧性能研究 张冬 陈振宇 齐舒 不同导热系数的挤塑板燃烧性能研究 张冬 陈振宇 齐舒( 福建省建筑科学研究院 福建省绿色建筑技术重点实验室 福建福州 350025) ［摘 要］ 对不同导热系数的挤塑板开展试验研究，获得其燃烧速率增长指数、600s 内总热释放量、600s 内总产烟量、烟气 生成速率指数、火焰横向传播等关键参数，探讨不同导热系数的挤塑板的燃烧性能。研究表明: 挤塑板遇火迅速熔融，并产生燃烧 滴落物。在本文的试验中，导热系数小的挤塑板发生剧烈的燃烧现象并产生大量的烟。导热系数较大的挤塑板则具有较好燃烧 性能。 ［关键词］ 导热系数 挤塑板 燃烧性能 单体燃烧 Study on Combustion Performance of XPS with Different Thermal Conductivity Abstract: This paper presented an experimental investigation on XPS with different thermal conductivity． Through the FIＲGA，THＲ600s， TSP600s，SMOGＲA，LFS and other parameters obtained from the experiment，the combustion performances of XPS with different thermal conductivity were then analyzed． The study concludes as follows: The XPS became rapidly molten under fire with flaming droplets in the combustion process． It is also proved that the XPS with lower thermal conductivity burnt heavily and produced lots of smoke，while the XPS with larger thermal conductivity had better combustion performance． Key words: thermal conductivity; XPS; combustion performance; Single Burning Item 0 引言 近年来，我国对建筑的节能要求日益加强。在 建 筑 物 外 墙和屋面增加保温层厚度在目前采用的主要手 段［1］。而 挤 塑板以其优良的保温性能和物理性能被广泛应用与现有的保 温工程。但挤塑板遇火易燃，在燃烧过程中会产生滴落物，且 燃烧滴落物也容易引燃其 他 材 料。例 如 2009 年 2 月 9 日 中 国中央电视台北配楼的火灾就是由于烟花点燃了建筑保温层 中的挤塑板引起的。而挤塑板在燃烧过程中不断产生滴落物 使得火势迅速蔓延［2］。因此，挤塑板的火灾危险性也受到广 泛的关注。 目前，已有一些学者对挤塑板的火焰蔓延特性、氧指数等 燃烧特性进行了研究，获得了一些有意义的成果［1 ～ 3］。但是， 这些研究并没有兼顾挤塑板的导热性能和燃烧性能。因此， 有必要将挤塑板的导热性能和燃烧性能联系起来，对其进行 分析，探讨二者之间可能存在的关系。 本文将针对不同导热系数下的挤塑板的燃烧性能进行试 验研究，对其燃烧速率增长指数、600s 内总热释放量、600s 内 总产 烟 量、烟气生成速率指数、火焰横向传播等参数进行分 析，研究不同导热系数下的挤塑板的燃烧现象，探讨挤塑板的 导热性能和燃烧性能之间的潜在关系，为其在生产和使用过 程中提供参考。 1 试验系统 试验采用建材制品单体燃烧试验装置 ( SBI) ，如 图 1 所 示。该装置的试验方法依据耗氧原理，可以模拟实际火灾场 景，同时具有较好的现实科学 性［1］。SBI 装 置可以测量试验 期间氧气浓度、二氧化碳浓度、烟气流量、光通量等关键参数 的变化。 试验采用纯度大 于 95% 的工业丙烷作为燃气。试 验 装 置中分别设有一个辅助燃烧器和一个主燃烧器，试样垂直安 装于主燃烧器附近 的 试 样 架 上。试 验 前 300s 为 试 验 准 备 阶 段和基准热释放速率测量阶段，仅点燃辅助燃烧器。300s 时 燃气切换至主燃烧器，由主燃烧器引燃试样。整个试验持 续 时间为 1560s，装置在 1560s 时自动切断燃气供应。试样暴露 于主燃烧器火焰时 间 为 1260s。但 试 验 仅 在 1200s 内 对 试 样 的性能进行评估［4］。试验