高熵合金制备方法进展.docxVIP

高熵合金制备方法进展 杨晓宁, 邓伟林, 黄晓波, 田林海 (太原理工大学 表面工程研究所, 山西 太原 030024) 摘 要：多主元高熵合金对传统的多元合金设计理念是一种新的突破，具有不同于传统合金的组织和性能。 阐述了 高熵合金的特性，介绍了近年来国内外关于高熵合金制备方法的研究现状及特点，以提高高熵合金的优良性能，拓宽其 应用领域。 关键词：高熵合金； 性能； 制备方法 中图分类号：TG132; TG146 文献标识码：A 文章编号：1001-3814(2014)22-0030-04 Research on Preparation Methods of High-entropy Alloy YANG Xiaoning, DENG Weilin, HUANG Xiaobo, TIAN Linhai (Institute of Surface Engineering, Taiyuan University of Technology, Taiyuan 030024, China) Abstract：The present of multi-principal element high-entropy alloys, which show different microstructure and properties with traditional alloys, is a new break for the traditional alloys design concept. To improve the performance of high-entropy alloys and broaden its application area, the preparation methods of the high-entropy alloy in China and abroad in recent years were introduced. Besides, the characteristics of high entropy alloys were described. Key words：high-entropy alloy; performance; preparation methods 针对合金体系的研究趋近于饱和的现状， 台湾 学 者 叶 均 蔚 [1] 于 1995 年 提 出 新 的 合 金 设 计 理 念———多主元高熵合金， 这对传统的多元合金设计 理念是一种突破。 多主元高熵合金一般由 5～13 种 主要元素组成， 且每种元素的摩尔含量介于 5%～ 35%。 该 合 金 在 热 力 学 上 具 有 很 高 的 熵 值 ( 大 于 1.61R)，动力学上具有原子迟缓扩散效应，晶体结构 上具有晶格扭曲效应， 此外多种元素的特性和它们 之间的复杂作用使高熵合金呈一种鸡尾酒效应[2]。 这些特性使高熵合金相比传统多元合金更不倾向于 形成金属间化合物且更易形成简单的固溶体结构和 纳米结构，甚至非晶质结构。 多主元高熵合金具有较高的强度， 良好的耐磨 性、高加工硬化，耐高温软化、耐高温氧化、耐腐蚀和 高电阻率等优异性能或这些优异特性的组合， 这是 传统多元合金所无法比拟的。 目前，多主元高熵合金在多个领域得到应用，如 可用作高速切削刀具、高尔夫球头打击面、油压气压 杆、钢管及辊压筒的硬面、高频软磁薄膜等。 高熵合 金所表现出来的优异耐蚀性能，使其在化学工厂、船 收稿日期:2013-10-23 作者简介:杨晓宁(1987- ),男,山西长治人,研究生,主要从事材料表面 改性方面的研究工作;电话 E-mail:yangxiaoning2007@163.com 舶等领域的应用也具有一席之地。 此外， 在电热材 料，除氢材料，在 IC 扩散阻绝层和微机电加工原件 等工业领域也有着较为广阔的发展前景。 1 制备高熵合金元素选择原则 高熵合金要求主元素种类在 5 种以上， 一般不 超过 13 种，元素过多易形成金属间化合物。 研究对 象 一 般 在 Al、Ti、V、Cr、Mn、Fe、Co、Ni、Cu、Zn、Mo 和 W 等元素中选配。 如使高熵合金形成固溶体还 需要在选配元素时考虑原子之间的电负性差异。 当 电负性相差很大时， 将形成化合物， 且在置换固溶 体时， 溶剂与溶质的溶解度会随着电负性的增大而 减小；原子之间的原子尺寸不能相差太大，原子半径 差小于 12%为宜，两种原子半径相差不大时，易于 形成固溶体结构，当原子尺寸相差很大时，晶格结构 坍塌，很容易形成非晶结构；所选元素之间的混