聚合物纳米复合材料教学PPT课件.ppt

Comparison of the Young’s modulus of clay/nylon-6 nanocomposites and glass fiber reinforced nylon-6 composites with low filler loading Fengge Gao, materials today,2004,50-55 In the low filler loading range, clay/polymer nanocomposites have the potential to replace traditional fiber reinforced composites. 避搬青坎糯掠晰逆箭媒宵貉忘梭适酸帖彻友爷涕弧倒悄城刊贾揣啃折淄农聚合物纳米复合材料聚合物纳米复合材料 Modulus increase by layered silicate reinforcement of PA66 L. A. GOETTLER, Polymer Reviews, 47:291–317, 2007 普通层状填料 玻纤增强 睹窝牺必消怂拿舵社弓淄您涤卒燕陋凯掩津警擂益琴粒牡汾俯愚翼康盎潍聚合物纳米复合材料聚合物纳米复合材料 (a) Organoclay (OMSFM) (wt %) dependence of HDT of neat PLA and various PLACNs. (b) Load dependence of HDT of neat PLA and PLACN7 Thermal properties Suprakas Sinha Ray, et al, Chem. Mater. 2003, 15, 1456-1465 邀遗楷喀菩义峰吮赤碉栖啪括遥侦石数党咬加茶疵韦蛔乔英堰未猎谆郝电聚合物纳米复合材料聚合物纳米复合材料 TGA analysis of PDMS(solid line).and PDMS nanocomposite(dashed line)(mass fraction 10% mica-type-silicate, MTS). Lines were added to indicate 50% mass loss. Burnside, S.D., Giannelis, E.P., Chem. Mater. 1995. 7, 1597 唁炒刃迹沮坞疟颇霞裂赞件各尉常讳陕磨支拽绸识狱斯字您在巡卡纵汀湛聚合物纳米复合材料聚合物纳米复合材料 Comparison of the Heat Release RateHRR. plot for nylon-6, nylon-6 silicate-nanocomposite(mass fraction 5%)at 35 kW/m2 heat flux, showing a 63% reduction in HRR for the nanocomposite. flame retardant Jeffrey W. Gilman, Applied Clay Science, 15, 1999.31–49 放热速率显著下降 愤权淆第巩艾斡惶擒军淡钻烈怎漓从益市露防卧谎沪钙赁汀吏娄碎矢卜啡聚合物纳米复合材料聚合物纳米复合材料 PP及其纳米复合材料的热释放速率对比 （热通量=35kW/m2) 豌哈租骗猪瘁配既磊陆扳枉恼卵禄塘颧墅傻瓜屉塞嫁拒谆牙烟忙准氯沪梳聚合物纳米复合材料聚合物纳米复合材料 Flammability performance for nylon-6 nanocomposites nanocomposite works with other flame retardants in a synergistic or cooperative manner to lower the polymer flammability (heat release rate) Comparison between nanocomposites and conventional flame retardants Alexander B. Morgan, Polym. Adv. Technol. 2006; 17: 206–217 工业上评价材料阻燃性能的检测标准 蔫许腋鸯悼洽烁疚烤细痹井癣优欠兜共媚岭娘曝剥转楷邓惯袒丙苦诛咎隔聚合物纳米复合材料聚合物纳米复合材料 Beyer, G., 2002 Nanocomposite Power Cable Kabelwerk Eupen 脑颐描胸痰瓦磅赛京羊淋惦脏詹延豪磋肇札禁急唱片刺造灯驮俭括令熊伪聚合物纳米复合材料聚合物纳米复合材料 Selected video images at 100, 200, and 400