PAGE II 题目：铝合金腐蚀速率的研究 铝合金腐蚀速率的研究 摘要 为了预防水、土壤、石油管道等环境中钢构的腐蚀采用牺牲阳极保护法，牺牲阳极保护是用于储罐防腐蚀的一种有效的技术措施，针对油田稠油污水对储罐的腐蚀性问题，开发新型的铝基牺牲阳极材料，铝基阳极比重小、电流效率高、发生电量大、对钢铁驱动电位适中、来源丰富,是一种迅速发展起来的新型牺牲阳极材料。本次试验主要对九种不同材料的浸润腐蚀的腐蚀速率的研究，通过质量损失法和腐蚀后形貌分析来表征九种牺牲阳极材料的腐蚀速率。 关键词：牺牲阳极材料；新型铝基阳极；质量损失法；形貌分析；腐蚀速率 Research on the?corrosion?rate of aluminum alloy Abstract In order to?prevent water, soil, oil pipelines and other environmental corrosion in steel sacrificial anode protection laws, sacrificial anode protection is an effective technical measures for tank corrosion, corrosion of tanks for heavy oil wastewater question, the development of new aluminum sacrificial anode material, a small proportion of aluminum anodes, high current efficiency, the occurrence of large capacity, moderate steel drive potential, a rich source of new sacrificial anode material is a rapidly developed. This test is mainly the corrosion rate of infiltration of nine different materials corrosion studies by mass loss method and the corrosion morphology analysis to characterize the corrosion rate of nine sacrificial anode material. Key words:?sacrificial anode?materials;?new aluminum?based anode;?mass loss method;?morphology analysis;?corrosion rate 目 录 TOC \o 1-3 \h \z \u HYPERLINK 1 绪论 1 HYPERLINK 1.1研究背景与意义 1 HYPERLINK 1.2 铝合金的腐蚀 2 HYPERLINK 1.2.1 金属腐蚀的电化学的基础 2 HYPERLINK 1.2.2 铝合金腐蚀的主要类型 3 HYPERLINK 1.3腐蚀速率的研究方法 6 HYPERLINK 1.3.1质量法 6 HYPERLINK 1.3.2失厚测量与孔蚀深度测量 6 HYPERLINK 1.3.3气体容量法 7 HYPERLINK 1.3.4电阻法 7 HYPERLINK 1.3.5极化曲线测量 7 HYPERLINK 1.4课题目的与意义 7 HYPERLINK 2 实验部分 11 HYPERLINK 2.1试验材料 11 HYPERLINK 2.1.1试验材料的加工与工艺 11 HYPERLINK 2.1.2试验用的腐蚀溶液根据稠油污水试样配置 11 HYPERLINK 2.2试验方法及表征手段 12 HYPERLINK 2.2.1质量损失法 12 HYPERLINK 2.2.2表征手段 14 HYPERLINK 2.3试验结果 15 HYPERLINK 2.3.1质量损失记录结果 15 HYPERLINK 2.3.2腐蚀后形貌 16 HYPERLINK 3 结果讨论 17 HYPERLINK 3.1腐蚀后形貌讨论 17 HYPERLINK 3.2腐蚀速率讨论 17 HYPERLINK 4 结论 19 HYPERLINK 参考文献 20