锂离子电池铝塑膜腐蚀的预测方法.docx

锂离子电池铝塑膜腐蚀的预测方法

刘亚明;王艳飞;黄磊;周朕良

【摘要】根据软包装锂离子电池中铝塑膜腐蚀行为发生的条件,研究铝塑膜腐蚀行为的预测方法.用氢氟酸(HF)对铝塑膜壳体进行腐蚀,再对聚丙烯(PP)层进行渗透剂喷涂的化学腐蚀法,可直观地判断铝塑膜PP层是否破损.根据电极与铝塑膜铝层间的电阻率计算实验电池的绝缘电阻,再用万用表测量铝塑膜绝缘电阻,发现PP层破损的电池,绝缘电阻低于计算值.使用化学腐蚀法和绝缘电阻测试法,可对软包装锂离子电池中铝塑膜腐蚀行为进行预测.%AccordingtotheconditionofaluminumlaminatedfilmcorrosionbehaviorhappenedinthepouchLi-ionbattery,theforecastmethodofcorrosionbehavioraboutaluminumlaminatedfilmwasstudied.ThemethodofchemicaletchingwhichusedHFtoetchthealuminumlaminatedfilmtocasecorrosion,thensprayedpenetratingagentontothepolypropylenelayer,couldbedirectlyusedtojudgewhetherthepolypropylenelayerwasdamaged.Themethodofusingthemetertomeasuretheinsulationresistancewhichwascalculatedaccordingtotheresistancebetweentheelectrodeandthealuminumlaminatedfilm,couldbeusedtodetectthebrokenpolypropylenelayerofthefinicalproduct.Theinsulationresistanceoffinicalproductwithbrokenpolypropylenelayerwaslowerthanthecalculatedvalue.ThecorrosionbehaviorofaluminumlaminatedfilminpouchLi-ionbatterycouldbeeffectivelypredictedbyusingchemicaletchingandinsulationresistancetestingmethod.

【期刊名称】《电池》

【年(卷),期】2017(047)001

【总页数】4页(P27-30)

【关键词】软包装锂离子电池;铝塑膜;腐蚀行为;化学腐蚀;绝缘电池测试

【作者】刘亚明;王艳飞;黄磊;周朕良

【作者单位】山东齐星新能源科技有限责任公司,山东邹平256200;山东齐星新能源科技有限责任公司,山东邹平256200;山东齐星新能源科技有限责任公司,山东邹平256200;山东齐星新能源科技有限责任公司,山东邹平256200

【正文语种】中文

【中图分类】TM912.9

软包装锂离子电池用铝塑膜从外到里主要分为尼龙层、铝层和聚丙烯(PP)层，层与层之间为黏合剂和黏合层[1]，具体结构见图1。

干法和热法工艺制作的铝塑膜，黏合剂和黏合层的分布及厚度略有不同。热法工艺制作的铝塑膜，黏合剂由3μm厚的胶黏材料组成，黏合层由10μm厚的改性PP组成。

尼龙层为装饰性层，主要起保护铝层不被刮伤的作用；铝层具有良好的耐穿刺性

能，能够起到铝塑膜成形和防止水分浸入的作用；PP层具有抗污染、机械强度高、耐有机电解液腐蚀的性能，能起到使铝塑膜严密热封的作用，还起到高温热封不短路的作用[1-2]。

由于铝塑膜封装过程是通过PP层进行热聚合，封装效果受温度、压力和时间的影响较大[3]，生产过程中设备运行不稳定、气压不稳定等都会影响封装效果，尤其

在能量密度达到700Wh/L以上的锂离子电池中。88μm、76μm铝塑膜的使用

已成为常态的情况下，运行参数的影响更加明显，出现不良品的几率和类别也多于较厚的其他型号的铝塑膜[4]。当这些外观和封装不良品不能被识别而混入正常产品进行流通使用时，就会发生铝塑膜腐蚀现象，导致电池气胀、漏液，产生一系列安全隐患。

预测铝塑膜的腐蚀隐患，对电池生产厂家至关重要，但本文作者尚未见到有关锂离子电池铝