宝钢高强度汽车大梁钢板宝钢技术中心汽车用钢研究所2007.9.

宝钢现有高强度大梁钢板性能指标牌号ReH(MPa)Rm(MPa)A(%)1800冷弯,弯心直径B510L≥355510~610240.5AB550L≥400550~650231.0AQStE380TM≥380450-590≥180.5aQStE420TM≥420480-620≥160.5aQStE460TM≥460520-670≥141.0aQStE500TM≥500550-700≥121.0a

牌号ReH(MPa)Rm(MPa)A(%)1800冷弯,弯心直径B510L450535290.5A合格B550L470580241.0A合格QStE380TM435505310.5a合格QStE420TM470540300.5a合格QStE460TM520580251.0a合格QStE500TM555630251.0a合格宝钢现有高强度大梁钢板实物水平（8mm)

国外高强度大梁钢板性能指标厂家EN10149-2机械性能SsabThyssenkruppEN10149-2ReH(MPa)Rm(MPa)A(%)1800冷弯,弯心直径Doxes700mcPAS700S700MC≥700750-950≥122.0aDoxes650mcPAS650S650MC≥650700-880≥122.0aDoxes600mcPAS600S600MC≥600650-820≥131.5aDoxes550mcPAS550S550MC≥550600-760≥141.5a

宝钢高强度大梁钢板技术指标宝钢高强度大梁钢板技术指标化学成分(wt%)级别(MPa)CSiMnPSAlNbVTi550≤0.10≤0.10≤1.70≤0.025≤0.010≥0.015≤0.09≤0.20≤0.15600≤0.10≤0.10≤1.80≤0.025≤0.010≥0.015≤0.09≤0.20≤0.15650≤0.10≤0.10≤2.00≤0.025≤0.010≥0.015≤0.09≤0.20≤0.15700≤0.10≤0.10≤2.10≤0.025≤0.010≥0.015≤0.09≤0.20≤0.15级别(MPa)屈服强度(MPa)抗拉强度(MPa)A(%)1800冷弯550≥550600～760≥14d=1.5a600≥600650～820≥13d=1.5a650≥650700～880≥12d=2a700≥700750～960≥12d=2a机械性能Nb+V+Ti≤0.22%

650MPa级大梁钢板实物水平650MPa级大梁钢板实物水平化学成分(wt%)0.06％C、1.64%Mn、微合金钢板机械性能厚度（mm）Rp0.2(MPa)Rm(MPa)A(%)冷弯368274821合格867076321合格868677023合格868276821合格1064374419合格1065175221合格－40℃冲击韧性钢板厚度（mm）Akv(J)试样尺寸8747.5×1010×55

宝钢高强度大梁钢板实物水平QStE550TM/B600L生产实绩化学成分：0.075％C、1.18%Mn、微合金钢板机械性能厚度（mm）Rp0.2(MPa)Rm(MPa)A(%)冷弯3.060568523合格3.558563522合格4.057563023合格

△QStE650TM/B700L生产实绩

化学成分：0.06％C、1.64%Mn、微合金

钢板机械性能厚度（mm）Rp0.2(MPa)Rm(MPa)A(%)冷弯3.068274821合格8.068276821合格10.064374419合格△QStE600TM/B650L生产实绩

化学成分：0.064％C、1.38%Mn、微合金

钢板机械性能厚度（mm）Rp0.2(MPa)Rm(MPa)A(%)冷弯16.060569522合格

B700L冲击韧性(－40℃)钢板厚度（mm）Akv(J)试样尺寸8747.5×1010×55

B700L冷弯性能8mm钢板3mm钢板3mm和8mm钢板双弯试验（d=0）

疲劳极限01.B700L02.热轧态钢板疲劳极限03.364.6MPa

B700L焊接接头疲劳极限315.4MPa

△ZQS700L/B750L生产实绩

化学成分：0.074％C、1.85%Mn、微合金

钢板机械性能厚度（mm）Rp0.2(M