含有Fe2+废水处理工艺的优化.pdfVIP

2007 中国钢铁年会论文集 含有 Fe2+废水处理工艺的优化 胡金良 吴志伟 丁铁锋 王建玲 (邯钢集团公司) 摘 要 在处理含有大量Fe2+ 的酸洗废水过程中，由于反应条件和操作等原因，造成废水出水中的SS COD 严重 超标。通过对这些因素的分析，我们采取了控制pH 值、加强废水循环和提高曝气时间提高废水中的溶解氧等措施， 解决了出水水质超标的难题。 关键词 氧化 沉淀效果 溶解氧 Improving the Process of Treating Waste Water With Lots of Fe2+ Hu Jinliang Wu Zhiwei Ding Tiefeng Wang Jianling (Han dan Iron and Steel Group Co. ) Abstract In the process of treating waste water from pickling line with lots of Fe2+, The quality of drain （SS，COD ） dose not meet the demand of the national standard because of reaction situation and operation. Through analyzing the causes , strictlier controlling PH of the waste water and making the waste water circulate and inflate to improve the concentration of dissolved oxygen in the waste water are applied in the treating waste water. At present, good effect of drain is get after solving the problems. Key words oxidate ，the precipitation effect ，dissolved oxygen 1 问题的提出 我厂废水处理站酸碱废水处理系统主要处理来自我厂酸洗线、酸再生站、脱盐水站、彩涂线和含油废水 处理系统的出水等酸碱废水。我厂废水处理站酸碱废水处理系统采用了酸碱中和絮凝沉淀化学处理法处理酸 碱废水。其中酸再生站和酸洗线的含酸废水中含有大量的 Fe2＋，由于在酸碱废水的调节池中的停留时间较 短，来不及充分氧化进入了中和反应池，形成Fe(OH)2 沉淀。在相同的停留时间条件下，Fe(OH)2 在斜板沉 淀池中的沉淀效果没有Fe(OH)3 的沉淀效果好，造成废水处理站出水水质的COD、SS 超标。为了解决这些 问题，我们对现有的工艺和操作做了调整和改进，使出水水质到达了国家二级标准。 2 废水处理站酸碱废水处理系统工艺 酸碱废水处理系统工艺流程图见图 1。 图 1 废水处理工艺流程图 含有 Fe2+废水处理工艺的优化 酸碱废水进水水质一览表见表 1。 表 1 酸碱废水进水水质 温度/ ℃ 自由酸/g ·L−1 SS/mg ·L-1 Fe2+/g ·L−1 Fe3+/g ·L−1 60 20～50 900 240 3 进水中的自由酸主要是来自漂洗水溢流和检修时排除的废酸或突然的设备故障排除的废酸，而且废酸中 的Fe2+是造成出水 SS、COD 超标的主要原因。 3 高浓度 Fe2+废水出水 S