钒微合金化HRB500高强度钢筋轧制与工艺改进.pdfVIP

钒微合金化 HRB500 高强度钢筋轧制与工艺改进 张亚军 王风才 (河北钢铁集团 邯钢公司 线棒材厂，邯郸 056015) 1 摘 要 利用高速线材轧机生产钒微合金化 HRB500 热轧钢筋的生产控制过程，通过钒氮微合金化及控轧控冷工艺 进行了低成本 HRB500 热轧盘条的试制，根据试制结果对工艺进行了优化设计，经过工业实践使成本进一步得到了 降低，工艺改进后减少了性能波动，同时避免了拉伸无屈服现象的发生，产品质量符合GB1499.2—2007 标准要求。 关键词 低成本 V 微合金化 HRB500 钢筋 Vanadium Micro Alloying HRB500 of High Strength Steel Rolling and Process Improvements Zhang Yajun Wang Fengcai (Coil-bar Plant,Handan Iron and Steel Company,Hebei Iron and Steel Group Company ,Handan, 056015) Abstract Using high-speed wire mill production vanadium HRB500 hot-rolled steel micro alloying control in the production of vanadium nitride process and by micro alloying and controlled rolling process of controlled cooling the low cost of HRB500 hot-rolled rod, according to the results of the trial process trial optimized design, after industrial practice make further reduce the cost, reduce the performance after process improvement fluctuations, avoiding the occurrence of tensile no yield phenomenon, product quality GB1499.2-2007 with standards. Key words low-cost,vanadium, micro alloying, HRB500, steel 1 引言 随着我国经济建设的需要，建筑结构对屈服强度大于 500MPa 的高强度钢筋的需求越来越大。HRB500 带肋钢筋广泛用于建筑工业、桥梁、水利枢纽大坝工程，在不改变结构承载能力的前提下，据有关数据统计， HRB500 钢筋用量比 HRB400 钢筋可减少 10%，为国家建科院优先推广产品。邯钢线棒材厂高线车间结合自 身设备特点，制定合适的生产工艺，成功生产出合格的 V 微合金化 HRB500 热轧带肋钢筋。针对线材生产 速度快，轧制温度高的工艺特点，采用了 V-N 微合金成分设计同时配以控制轧制温度和冷却工艺开发了 HRB500 热轧盘条产品。 钒作为贵金属资源使 HRB500 盘条的成本提高，在满足钢筋性能要求的前提下，通过优化控制轧制及 冷却工艺，应尽可能减少钒的加入量，达到节约钒资源和减少合金成本的目的。 2 工艺流程 120t 转炉→LF 精炼→方坯连铸→高线车间加热→粗轧→飞剪切头→中轧→预精轧→精轧→水箱控冷→ 吐丝机→散卷辊道→集卷→P/F 运输机→取样→打捆→称重→挂牌→卸卷→入库。 张亚军（1981— ），男，2006 年毕业于内蒙古科技大学材料成型专业，现在河北钢铁集团邯钢公司线棒材厂工作，xbccscjsk@mail.hgjt.cn 钒微合金化HRB500 高强度钢筋轧制与工艺改进 3 成分及工艺设计 3.1 成分设计 按