  热处理后 GO/MnO2 电极材料微观结构对电 容增效的影响# 王令云，王勇，王晓敏** 5 10 15 20 25 30 35 40 （太原理工大学材料科学与工程学院，太原市（030024）） 摘要：不同温度下热处理氧化石墨烯(graphene oxide, GO), 并按 20wt%含量将其与 MnO2 复合, 制得 GO/MnO2 复合材料。 采用扫描电镜(SEM), X 射线衍射(XRD)及傅里叶红外(FT-IR)表征分析了复合材料的 表面形貌与结构, 四探针测试了其电导率, 并通过循环伏安测试计算得到了复合材料的比电容。 结果表明, 600 热处理后的 GO 与 MnO2 复合得到的材料比电容最高, 为 321 F·g-1, 相较于纯相 MnO2 提高了 87%。 热处理 GO 在改善其导电性的同时, 残留的含氧官能团还提供了赝电容, 使 GO 和 MnO2 形成了协同效应。 关键词：氧化石墨烯/MnO2 复合材料；比电容；热处理；官能团 中图分类号：O646 Promotion Effect of GO/MnO2 Microstructure after Heat Treatment on the Capacitance of the Composite Material WANG Linyun, WANG Yong, WANG Xiaomin (College of Material Science and Engineering,Taiyuan University of Technology,Taiyuan(030024)) Abstract: Graphene Oxide (GO) was heated in different temperatures, and mixed with MnO2 in 20wt% to form GO/MnO2 composite materials. The morphology and structure of the materials were characterized by scanning electron microscopy (SEM), X ray diffraction spectrometry (XRD) and Fourier Transform Infrared Spectrometer (FT-IR). The electrical conductivity was tested with a four-probe method. Meanwhile, the specific capacitance was calculated from the curve of the Cyclic Voltammetry. Results show that the GO/MnO2 composite materials with 600 ℃ reduced GO as a component have the highest specific capacitance of 321 F·g-1, which is 87% promoted compared with the pure MnO2. As the electrical conductivity is improved after the heat treatment, the left oxygen-containing functional groups still provide faradaic pseudocapacitance, making it good synergetic effect between GO and MnO2. Key words: GO/MnO2 composite material; Specific capacitance; Heat treatment; Functional groups 0 引言 MnO2 因其具有较高的赝电容，低廉的价格，友好的环境相容性，已成为替代贵金属氧 化物作为超级电容器材料的研究热点[1, 2]。如 Devaraj 和 Munichandraiah[3]利用过量的 KMnO4 氧化 MnSO4 制备了比电容为 236 F·g-1 的 MnO2. Yang 和 Huang[4]利用水热法制备的 MnO2， 其比电容达到了 259 F·g-1。但是 MnO2 固有的电导率低，易团聚的缺点使得其电容仍难以达 到实际应用的要求[5]。研究者们尝试采用将 MnO2 与导电性能好的炭材料复合[6, 7]，以提升 电容性能。如 Wang 等[8]利用碳纳米管比表面积大和导电性好的优点，将其与采用 KMnO4 氧化法得到的