岩藻聚糖硫酸酯-胶原复合支架的制备及其性能研究.pdfVIP

中国科技论文在线 岩藻聚糖硫酸酯-胶原复合支架的制备及其 性能研究# 易静楠，曹佳琳，毛萱，王小莺，汤顺清** 5 （暨南大学生物医学工程研究所，广州 510632） 摘要：该研究以冷冻干燥法制备了岩藻聚糖硫酸酯-胶原共混支架材料，对其进行扫描电镜、 吸水率、体外降解性能、细胞毒性检测和分析，以及与成纤维细胞复合共培养，检测细胞在 材料上的生长情况。结果表明：岩藻聚糖硫酸酯-胶原共混支架材料具有一定孔径的网状结 构，有良好的生物相容性，细胞能粘附在材料上生长。可作为一种潜在的生物材料可望在生 10 物医学领域得到应用。 关键词：岩藻聚糖硫酸酯；胶原；支架材料 中图分类号：O 636.1 Preparation and characterization of fucoidan-collagen 15 scaffold YI Jingnan, CAO Jialin, MAO Xuan, WANG Xiaoying, TANG Shunqing (Institute of Biomedical Engineering, Jinan University, GuangZhou 510632) Abstract: :Fucoidan/type I collagen scaffold was prepared successfully by freeze-drying process and its structure and properties including pores, water absorption, cell toxicity, in vitro 20 degradation rate were characterized . Fibroblasts culture with the scaffold, and found it proliferated very well on the scaffold. These results showed that the fucoidan/type I collagen scaffold with certain pore size had good compatibility, and fibroblasts can attach and proliferate on the scaffold. These performances show fucoidan/type I collagen has a promise as a new type of biomaterial. 25 Keywords: fucoidan; collagen; scaffold 0 引言 皮肤修复一直是个古老且未完全得到解决的问题。由于皮肤损伤一般不能自动愈合，除 非用一些皮肤替代品辅助再生，否则疤痕的形成将不可避免。多年来许多皮肤替代品已经应 30 用于皮肤损伤，如异种移植，同种异体移植，自体移植。但由于免疫源性、供体来源有限等 [1-5] 问题，这些皮肤替代品未能满足需要 。组织工程皮肤是组织工程研究最为成熟的一个领 域，其核心内容是构建一种支持细胞生长的三维支架，与角质形成细胞或成纤维细胞进行体 外复合培养，形成可用于创面覆盖与修复的皮肤等同物[6]