热压型地板基材用无醛胶黏剂的研究.pdfVIP

热压型地板基材用无醛胶黏剂的研究 王淑敏1’2时君友2★祖游行2 (1．东北林业大学，2．北华大学术质材料科学．!-jI程省重点实验室，吉林132013) 摘要：本研究以乳液与PVA的配比、乳液的种类为变量，所合成的胶黏剂压制的三层 胶合板的胶合强度为考核指标米设计正交实验，优化出变量的最佳值。试验结果表明， 变量对胶合强度的影响显著。在优化条件下压制的胶合板理化性能符合 效益。 关键词：胶合板；无醛胶黏剂；湿胶合强度 on adhesivein floor substrate Studynon—formaldehydehot-press Shumin Zu Wang，JunyouShi，Youxing lab．ofwoodenmaterialscienceand (1．NortheastForestryUniversity,2．Provincialkey engineering， Beihua 32013) University,JilinCity,1 to AbstractsThe testwas theratiooflatex oflatexforvariableand orthogonaldesignedby PVA，type for was of examinationindex．Thevariable test bondingstrengththree-layer optimized．The plywood resultshowedthatthe on Was effectofvariable andchemical bondingstrengthprominent．Thephysical of this conditionmeet cost propertiesplywoodpressedby optimized GB／T9846-2004．Theofadhesive lowered1 totheconventionalAPI has economic 2％compared adhesive，whichgood benefit． Keywords：plywood；non·formaldehydeadhesive；wetbondingstrength 甲醛系胶黏剂有一个致命的缺陷，由于其主要原料之一为甲醛，用其胶接木材制 品在长期生产过程与使用过程中不可避免的会释放出游离甲醛等有害气体，从而危害 生产者与产品消费者的身体健康。水性高分子异氰酸酯胶黏剂，简称API(无醛胶) []。随着人们对安全意识和环保意识的增强，甲醛的释放越米越受到关注，同时也影 响了人造板的销售。因此，开发环保型的胶黏剂，重点开发无甲醛型胶黏剂成为大势 所趋。 本论文主要是解决目前国内热压型地板生产线上所用的无醛(API)胶黏剂的活 性期短，结膜速度快，开口陈放时间短，工艺性能差等缺点，通过实验优化出