以废弃聚苯乙烯泡沫板为原料制备聚苯乙烯空心微球.pdfVIP

· 94 · 材料导报 ：研究篇 2010年 1月(下)第 24卷第 1期 PreparationofHollow M icrospheresfrom W asteFoamedPolystyrenePlastics~ ControlofTapDensityandAverageDiameter WEIBin，WANGShujun，LIU Hongyan，LIUNing (1 StateKeyLaboratoryofHeavyOilProcessing，ChinaUniversityofPetroleum，Beijing102249；2 Instituteof ChemicalScienceandEngineering，ChinaUniversityofPetroleum，Beijing102249) Abstract W astefoamedpolystyreneplasticisusedasthemainraw materialforthepreparationofpolystyrene hollow microsphereswithhighadditionalvaluebymicroencapsulationmethod．Thefactorssuchasthemassratioof water／oilphases，thefirstandsecondemulsifyingrotatingspeed，theconcentrationofemulsifierinW1一phaseandthe concentrationofpolystyrenein()-phaseonthetapdensityandaveragediameterofpolystyrenehollow microspheresare studied．Onthisbasis，polystyrenehollowmicrosphereswiththelowesttapdensityof0．1lg／cmaandaveragediame- terbetween75～646“m aresuccessfullyproduced．Finallythispapergivesbriefintroduction toscale-upexperiment anddiscussiontotherecyclingtechnologyofreagentsusedinexperimentofscaleuptechnology．Theresultsindicate thatthetechnologyisfeasibleandprovideastrongbasisfortheequipmentdesignofindustrialunitortheexploration ofprocesstechnology． Keywords wastefoamedpolystyreneplastics，polystyrenehollow microspheres，microencapsulationmethod， tapdensity，averagediameter 以废弃聚苯 乙烯泡沫板为原料制备聚苯 乙烯空心微球 魏 斌 ，汪树军 ，刘红研 ，刘 宁 (1 中国石油大学重质油国家重点实验室，北京 102249；2 中国石油大学化学科学与工程学院，北京 102249) 摘要 以废旧聚苯乙烯泡沫板为成球材料，采用微封装法制备 了具有高附加值的聚苯乙烯空心微球。考察了 水油相质量 比、第 1次和第 2次乳化搅拌速度、第一水相中乳化剂浓度和油相中聚苯乙烯浓度对聚苯乙烯空心微球 振实密度及平均直径的影响。在此基础上，制备 出最低振 实密度为 0．1lg／cm。、粒径为 75~646m 的不同平均直径 的聚苯乙烯空心微球。最后简