锂离子电池硅基负极材料表面掺杂研究.pdfVIP

第30届全国化学与物理电源学术年会 锂离子电池硅基负极材料表面掺杂研究 卢志威，彭庆文，许寒，刘兴江 （中国电子科技集团公司第十八研究所，化学与物理电源技术重点实验室，天津，300384 ） 摘要：在本文中，我们制备了 Si-C 复合电极材料，并对其进行了表面掺杂。发现 Li O 的掺杂可以有效的提高材 2 料的电化学容量；而 Al2O3 的掺杂则可以提高材料的循环性能。 关键词：硅碳复合材料；负极材料；表面掺杂；电化学性能 Electrochemical performance of surface doped Si-composite negative material for Li-ion batteries Zhiwei Lu, Qingwen Peng, Han Xu, Xingjiang Liu (Science and Technology on Power Sources Laboratory, Tianjin Institute of Power Sources, P.O.Box 296, Tianjin 300384, China) Abstract: Si-C composites are synthesized by ball-milling the mixture of Si, graphite ,coal pitch and a little amount of acetate, and subsequent heat treatment at 900 ºC in inert atmosphere. The electrochemical performance and microstructure of the composites are investigated. The electrochemical tests indicate that a little amount of Li2O can efficiently enhance the electrochemical capacity of the Si-C; at the meanwhile, the cyclic behavior of Si-C composite can be improved by doped by a little amount of Al O . 2 3 Keywords: Si-C composites, negative material, surface doped, electrochemical performance 1.引言 锂离子电池因其高比能量，无污染，应用范围得到了飞速发展，已从移动通讯电源、笔记本电脑、摄像机 等扩大到电动工具、电动汽车等领域。而现有的碳负极的电化学容量偏低，不能满足科技发展的对便携二次电 池性能的进一步要求。目前，Si 材料由于其电化学可逆容量高，安全性好，资源丰富等优势，已成为锂离子二 次电池负极材料的首选材料。作为锂离子电池的硅基材料具有极高的理论电化学容量。但硅基材料在电化学嵌 锂过程中的体积变化过大，首次充放电效率较低，严重阻碍该电极材料的实际应用。目前，硅材料的应用研究 一般采取各种方法，使活性物质硅的粒度减小至纳米尺度，以减小其电化学嵌锂反应过程中的内应力变化，同 时包覆以高导电性材料（主要为碳材料和部分金属材料），以提高材料的稳定循环性能。 在本文中，我们发现，Si-C 复合材料的表面状态同样对硅材料的循环性能有很大的改善作用。在实验中， 我们添加了少量的 Li O 和 Al O ,对 Si-C 材料进行了表面改性，取得了一定的进展。其机理正在研究中。 2 2 3 2.实验 将一定比例的硅、石墨、煤沥青材料，以及醋酸锂、醋酸铝在有机溶液中在Fritsch P-5 型球磨机进行球磨处 理，球磨时间 20 小时，球料比 15：4 . 球磨后的样品经真空烘干，抽离溶剂，得