提高双刚体振动磨的磨碎效率地研究.pdfVIP

第八届全国振动理论及应用学术会议论文集，上海，2003 年 11 月 提高双刚体振动磨的磨碎效率的研究 侯书军，秦志英，彭伟，张新聚 (河北科技大学振动工程研究所，石家庄，050054) 摘 要： 双刚体振动磨为我们新发明一种新结构振动磨，它首次实现了振动能量的双向输入，彻底消除 了中心低能区的影响，为振动磨的发展奠定了基础。本文对其进行了理论与试验分析，对该类新型磨机的最 优工艺参数进行了初步探索，得出了一些有益的结论。 关键词： 双刚体振动磨；低能区；相对运动轨迹；能量输入 Improving the Grinding Efficiency of the Double-Rigid-Body Vibration Mill HOU Shu-jun, QIN Zhi-ying, PENG Wei, ZHANG Xin-ju (Insitute of Vibration Engineering, Hebei University of Science and Technology, Shijiazhuang, 050054) Abstract: Vibration mill with double-rigid-body is a newly developed vibration mill, which can input impact energy to the charges in the grinding tube from two opposite directions: from the wall inward and from the central rigid body outward into the charges in the tube. It, therefore, provides a rigid base for the further development of the vibration milling techniques. In this paper, it was investigated both numerically and experimentally, the optimal processing parameters have been obtained. key words: Double-rigid-body vibration mill; Low energy zone; Relative movement orbit; Energy input 基金资助：河北省教育厅博士基金项目（B2001208），河北省自然科学基金项目（501246 ） 作者简介：侯书军（1963－），男，河北鹿泉人，教授，博士 1 1 引言 新材料科学技术，特别是纳米科学技术的发展，对超细研磨设备提出了更高要求：产品平均粒度更 细、粒度和相变微观结构更均匀。振动管磨机是能够制备超细（微米级）、超微粉体（亚微米和纳米级） 的设备之一，但传统振动磨存在的中心低能区问题[1-3] ，不仅使之难于满足上述要求，而且筒径越大该问 题越突出，严重制约了振动磨的大型化和在更广泛的领域内的应用。可以认为，传统振动磨产生中心低 能区的根本原因是，振动能量从磨管壁向管内的磨介和物料的单向输入，此时，因能量传递过程中的耗 散，磨介间碰撞能量从外到里必呈外高内低的指数衰减规律，当管径较大时（如超过 650 mm ），中心区 必然发展成为不能进行有效破碎的低能区。因此，要从根本解决中心低能区问题，必须改进能量的输入 方式。 图 1 所示为我们提出的一种新型振动磨——双刚体振动磨[5] ，侯书军等[6-8]对其原理和性能进行了初 步分析，但是，欲使磨机工作于最佳状态，就必须对影响磨机性能的主要因素，包括工作频率、磨介充 填率、物料充填率等进行试验研究[4] 。本文主要对这些因素的影响规律进行了试验和机理研究，为双刚体 振动磨的工业应用奠定了基础。 2 试验装置和试验参数 2.1 试验机型： （1） 如图 1 所示，用此样机作为双刚体振动磨 的实验机型。