国产热轧改进型ICDP工作辊的性能和使用研究.pdfVIP

国产热轧改进型 ICDP工作辊的性能与使用研究 彭 辉 宝钢股份公司设备部 摘要 通过对不同厂家的轧辊进行金相组织及使用性能的对比与分析 明确了国产改进型ICDP工作辊的发展方向 通过加稀土元素及强碳 化物形成元素 对确定的化学成份进行试浇轧辊并进行耐磨性等性能的分析 还检验了从表面到芯部的基体组织 碳化物及石墨连续变化 金相组织 根据使用实绩 总结出国产改进型ICDP辊的特点是耐磨性和抗事故性兼优 属于综合强化型的新型 ICDP轧辊 关键词 综合强化型 ICDP磨损 抗事故性 基体组织 碳化物 石墨 稀土元素 The properties and usage research of enhanced ICDP work rolls made by local roll maker for hot rolling mill Peng Hui (Equipment Department of Baoshan Iron Steel Co., LTD) Abstract: With the comparison in microstructure and performance, different rolls have been analyzed. The direction for new ICDP grade has been decided. Adding the lanthanide and carbide-formed elements, the cast roll rings for research have been made, also the wear resistance testing has been carried out. The evolvement of matrix, carbide and graphite from the roll surface to core material have been showed. According to the performance, it is can easily be summarized that the enhanced ICDP rolls must have the good wear resistance and accident resistance, that means, it must has the better integrated properties than the normal ones. Key words: integrated enhanced ICDP, wear, accident resistance, grey spots, matrix, carbide, graphite, lanthanide, oxide film 1 前言 随着轧辊技术的进步 宝钢热轧精轧F1-5机架工作辊已全部或部分由高铬铸铁改为高速钢材 质 相应成品前架 F6及成品架 F7的原普通高镍铬无限冷硬铸铁工作辊 以下简称普通ICDP 辊 材质工作辊 在使用至小直径时 已不适应高表面质量热轧板卷要求 目前国际上普遍使用改 进型 ICDP辊 宝钢也逐步扩大改进型ICDP辊的使用 至03年 进口辊已全部为改进型 ICDP辊 由于国内外改进型ICDP辊采购差价高达30-40%本着降低成本 满足钢材生产需求的目的 进行了改进型 ICDP辊的国产化工作 初步使用结果表明 本土化轧辊在 1580机组达到了进口辊实 物水平 2 前期工作 2.1进口辊检验分析 课题组对目前在宝钢使用的进口改进型 ICDP轧辊实物进行了检测 内容包括金相组织及硬度 等 金相组织包括辊身碳化物 石墨 基体组织 并根据检测情况确定了国产化的方向及目标 2.1.1金相组织检测情况 以下是使用实绩良好的国外A厂的金相检测结果 辊身 石墨 小团及团虫状石墨 数量少 如图 1所示 组织 贝