残余奥氏体对滚动轴承疲劳寿命影响.pdfVIP

材料热处理技术 Material Heat Treatment 年 月 2010 5 残余奥氏体对滚动轴承疲劳寿命的影响 钱 坤 杭州职业技术学院 浙江 杭州 ( , 310018) 摘 要：分析滚动轴承表面疲劳剥落失效机理和残余奥氏体对疲劳寿命的影响，确定控制残余奥氏体含量的热处 理工艺，进行残奥量测试与轴承疲劳寿命试验。 结果表明，残余奥氏体含量为 12%时，轴承的疲劳寿命较高。 关键词：滚动轴承； 热处理工艺； 残余奥氏体； 疲劳寿命 中图分类号： ； 文献标识码： 文章编号： TG156 TG162.71 A 1001-3814(2010)10-0060-02 Influence of Retained Austenite on Fatigue Life of Rolling Bearing QIAN Kun (Hangzhou Vocational Technical College, Hangzhou 310018, China) ： Abstract The fatigue spalling failure mechanism of rolling bearing surface and the influences of retained austenite content on the worklife of bearing fatigue spalling were analyzed. The heat treatment process for controling the retained austenite was content determined. The tests on the retained austenite content and bearing fatigue life were carried out. The results show that the worklife of the rolling bearing is longer when retained austenite content 12%. ： Key words rolling bearing; heat treatment process; retained austenite; fatigue life 随着高速精密加工技术的发展， 电机与主轴为 通过对不同润滑介质轴承的失效方式的深入分 实现高速精密加工而成为机床的“芯片”部件，与之 析， 对残余奥氏体能大幅度提高在污染环境中轴承 相配套的精密滚动轴承的研究与应用成为关键技 的使用寿命有了新的认识。 在污染环境中使用的轴 术。 精密轴承在高速运转中， 不仅要求高的运转精 承主要是以表面起源的接触疲劳剥落而导致最终失 度、 低的噪音，更要有长的轴承使用寿命和高的可 效。 其失效的机理如下，在污染的润滑介质中，硬粒 靠度。 如何提高滚动轴承的疲劳寿命，成为各大轴