硫含量对中碳钢高温力学性能的影响.pdfVIP

硫含量对中碳钢高温力学性能的影响 秦 哲 严国安 孙彦辉 田志红 许中波蔡开科 (北京科技大学) 度和塑性，扫描电镜分析结果表明，随着硫含量的增加，细小的夹杂物MnS在奥氏体晶界优先析出，降低了晶间的 结合强度，高硫钢比低硫钢的高温塑性RA降低了19．92％，高温抗拉强度％降低了4．75N／mm2。 关键词：硫含量高温塑性高温强度 Effectof ContentonMechanicalBehavierUnder Sulfur forMediumCarbonSteel HighTemperature ZheYanGuoanSunYanhuiTian Xu CaiKaike Qin ZhihongZhongbo of and Science (University TechnologyBeijing) for and 45 steel(S=0．016％)andsteel(S=0．059％)was Abstract：Hightemperaturestrengthductilityrolling casting Gleeble RA testedathermalstress／strainsimulator 1500．Theresultshowthatthe and by hightemperatureductility tensile of sulfurcontentsteelreduced19．92％and4．75N／mm2 with hightemperaturestrengthhigh separatelycompared thelowsulfurcontent reasonisthatthefineinclusionMnSwasfirst ontheaustenitiebound— steel，the precipitated gram anddecrn嘲xlthecombined ary strength content Key瞄：sulfurhight锄pl鼬tureductilityKght匿nperaturestrength 1引言 8000C、850℃、900℃、1000*C、1 改善钢的切削加工性能已得到人们广泛的关注。 1350℃、1400℃)，保温308后以1．0×10—3／s的应变 为提高钢的切削性能，向钢中添加了易切削元素S、 速率进行拉伸试验。 Pb、Ca等。其中向钢中加入S元素以改善钢的切削性 表1试验钢的化学成分(％) 能已经得到了较多的运用。但是，硫在改善钢的切削 性的同时恶化了钢的力学性能，尤其是横向性能。文 钢种 C sl Mn P S Ca A15 献[1～2]研究了硫对钢力学性能的影响，而硫含量对 X1 0．46 O．2l 0．66 0．030．0160．00110．007 钢的高温性能的影响目前在国内研究报道很少。本试 X2 0．4l 0．460．72 0．020．