ActiveandPassiveElec.Comp.,2002,Vol.25,pp.191–199 BME-Y5V MATERIALS PREPARED BY SOLID STATE TECHNOLOGY* G.KOEBRUGGE{,K.ALBERTSENzandI.HAYASHI} FerroElectronicMaterialsB.V.Frontstraat2,5405PBUden (ReceivedNovember2001) InthispaperthepropertiesofBME-Y5Vdielectricpowderspreparedbysolidstatetechnologyisdescribed.Anew formulation is presented, suitable in multilayer capacitors for layers down to 4mm. The material shows good reliability due to the presence of magic dopants in this formulation. The effect of magic dopants in dielectric formulationsisdiscussed. Keywords: Dielectricpowders,multilayercapacitors,ceramicpowders INTRODUCTION In the ?eld of Y5V multilayer capacitors the production share of parts with base metal electrodes (BME) has been increased tremendously[1] since their ?rst introduction ca. 10 yearsago[2].Thereareprojectionsthatin5yearsthemarketforY5VMLCsusingnoble metalelectrodeswillbenegligible[1]. Ferro Electronic Materials has more than 7 years experience in industrial production of mixed oxide based BME-Y5V powders and was the ?rst company to offer ready to use formulationstotheMLCmakers. InthispaperwearegoingtodescribethepropertiesofdielectricpowdersforBME-Y5V MLCs for different dielectric layer thickness applications. Especially in order to allow the production of thinner dielectric layers to obtain higher volume capacities a new dielectric materialwillbepresentedthatisinthe?nalstagesofdevelopmentandwillsoonbereleased forevaluationatcustomers. *An earlier version of this paper was published in the Proceedings of the 15th Annual European Passive ComponentsConference(CARTS-EUROPE2001),15–19October2001,pp.206–209. {Correspondingauthor.E-mail:gerald.koebrugge@ z } E-mail:knuth.albertsen@ E-mail:isao.hayashi@ ISSN0822-7516print;ISSN1563-5031online#2002TaylorFrancisLtd DOI:10.1080/0882751021000001582  192 G.KOEBRUGGEetal. EXPERIMENTAL 1 MixedOxidePreparation Basedonadvancedhighpurityrawmaterialsandasophisticatedproductionprocessthatis designedtoavoidc